Fast Curing of Carbon Fiber Reinforced Plastics Using the Integration of Nanoparticles

Abstract:

Fast curing of carbon fiber reinforced plastics (CFRPs) is limited by the degradation of the resin under high temperatures and by the development of internal strains. The authors counter these problems by adding nanoparticles to the matrix of CFRPs. In the presented work various volume fractions of nanosized aluminum oxide particles are integrated into the epoxy resin RTM6. To demonstrate the increased heat flow within the CFRP component, thermal conductivity tests are presented. Results show increasing values as the filler content is raised.With increasing filler content the reaction speed is also accelerated. This effect is analyzed by differential scanning calorimetry. It is shown that the particle surface has a catalytic effect on the curing of the epoxy resin. The results of the author also show that the added nanoparticles not only change the material composition, but also modify the network of the epoxy resin. In a series of experiments it is demonstrated how nanoparticles decrease the chemical shrinkage. The results show a reduction of the shrinkage higher than the volume fraction of the nanoparticles, which can be explained by the formation of interphases. Thermal mechanical analysis also confirms a decreased thermal shrinkage due to the integration of nanoparticles. Finally, the inspection of L-shaped CFRPs samples with different filler contents show the ability of nanofillers to decrease the spring-in.In summary, the integration of aluminum oxide decreases the thermal as well as the chemical shrinkage, increases the thermal conductivity and accelerates the chemical reaction.Overall, these changes in curing behavior lead to an increased dimensional stability of the CFRPs. Thus, nanoparticles may be one way of overcoming the disadvantages of fast curing cycles.

• Periodical: Materials Science Forum (Volumes 825-826)
• Pages: 3-10
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.825-826.3
• Online since: July 2015
• Authors: Wibke Exner*, Mark Opitz, Peter Wierach
• Keywords: Aluminum Oxide, Carbon Fiber Reinforced Plastics, Cure, Kinetic, Mechanical Properties, Nanocomposites, Shrinkage

References

[1] C. Heinrich, M. Aldridge, A. S. Wineman, J. Kieffer, A. M. Waas, K. W. Shahwan, Generation of heat and stress during the cure of polymers used in fiber composites, International Journal of Engineering Science, 53 (2012) 85-111.

DOI: 10.1016/j.ijengsci.2011.12.004

[2] H. Koushyar, S. Alavi-Soltani, B. Minaie, M. Violette, Effects of variation in autoclave pressure, temperature, and vacuum-application time on porosity and mechanical properties of a carbon fiber/epoxy composite, Journal of Composite Materials, 46(16) (2011).

DOI: 10.1177/0021998311429618

[3] E. Poodts, G. Minak, L. Mazzocchetti, L. Giorgini, Fabrication, process simulation and testing of thick CFRP component using the RMT process, Composites: Part B, 56 (2014) 673-680.

DOI: 10.1016/j.compositesb.2013.08.088

[4] S. Duwe, C. Arlt, S. Aranda, U. Riedel, G. Ziegemann, A detailed thermal analysis of nanocomposites filled with SiO2, AlN or boehmite at varied contents and a review of selected rules of mixture, Composites Science and Technology, 72 (2012).

DOI: 10.1016/j.compscitech.2012.04.015

[5] B. Weidenfeller, M. Höfer, F.R. Schilling, Thermal conductivity, thermal diffusivity, and specific heat capacity of particle filled polypropylene, Composites: Part, A 35 (2004) 423-429.

DOI: 10.1016/j.compositesa.2003.11.005

[6] J. M. Svanberg, J. A. Holmberg, An experimental investigation on mechanisms for manufacturing induced shape distortions in homogeneous and balanced laminates, Composites: Part A, 32 (2001) 827-838.

DOI: 10.1016/s1359-835x(00)00173-1

[7] M. R. Wisnom, M. Gigliotti, N. Ersoy, M. Campbell, K. D. Potter, Mechanisms generating residual stresses and distortion during manufacture of polymer-matrix composite structures, Composites: Part A, 37 (2006) 522-529.

DOI: 10.1016/j.compositesa.2005.05.019

[8] M. Holst, Reaktionsschwindung von Epoxidharz-Systemen, dissertation, University Darmstadt, (2001).

[9] Y. K. Kim, I. M. Daniel, Cure Cycle Effect on Composite Structures Manufactured by Resin Transfer Molding, Journal of Composite Materials, 36(14) (2002) 1725-1743.

DOI: 10.1177/0021998302036014598

[10] S.R. White, H.T. Hahn, Cure Cycle Optimization for the Reduction of Processing-Induced Residual Stresses in Composite Materials, Journal of Composite Materials, 27 (1993) 1352-1378.

DOI: 10.1177/002199839302701402

[11] N. Ersoy, K. Potter, M.R. Wisnom, M.J. Clegg, Development of spring-in angle during cure of a thermosetting composite, Composites: Part A, 36 (2005) 1700-1706.

DOI: 10.1016/j.compositesa.2005.02.013

[12] D. Hoebbel, M. Nacken, H. Schmidt, The Effect of nanoscaled Metal Oxide Sols on the Structure and Properties of Glycidoxypropyltrimethoxysilane Derived Sols and Gels, Journal of Sol-Gel Science and Technology, 19 (2000) 305-309.

DOI: 10.1023/a:1008777414416

[13] J. Gonzalez-Bendito, E. Castillo, J. F. Caldito, Coefficient of thermal expansion of TiO2 filled EVA based nanocomposites. A new insight about the influence of filler particle size in composites, European Polymer Journal, 49 (2013) 1747-1752.

DOI: 10.1016/j.eurpolymj.2013.04.023

[14] X. Chu, R. Huang, H. Yang, Z. Wu, J. Lu, Y. Zhou, L. Li, The cryogenic thermal expansion and mechanical properties of plasma modified ZrW2O8 reinforced epoxy, Materials Science and Engineering A, 528 (2011) 3367-3374.

DOI: 10.1016/j.msea.2011.01.003