pvT-Behavior of Polymers under Processing Conditions and Implementation in the Process Simulation

Abstract:

The development of high performance products at lowest possible product development-time and costs is the demand of the plastics industry today. A successful use of process simulation to describe the behavior of complex structures and to minimize the technical and economic risks for companies requires application and process-relevant material data.The pvT-behavior of polymers is an essential parameter for process simulations. Especially the dependence of the specific volume of pressure and temperature [1, 2] under process conditions is not mapped to the existing measurement methods.In this study pvT measurements were performed on selected amorphous and semi-crystalline polymers (PP, HDPE, POM, PBT, and ABS) with a Pirouette pvT device, a combination of a dilatometer and Couette rheometer. The specific volume was determined as a function of temperature (25-300°C) and at pressures ranging between 200-1000 bar. On top of that, the influence of the cooling rate was also investigated by pvT measurements performed at cooling rates of 0.1°C/s, 1°C/s and 100°C/s.The coefficients for the 2nd domain Tait pvT-model, which is implemented in the software Autodesk Moldflow, were determined by fitting the experimental pvT data and comparing them with the measured curves. As a result, the semi-crystalline polymers show a shift of the transition temperature to lower temperatures and a reduction in the specific volume in the melt is observed. For validation, in a case study shrinkage results in real were compared with the simulation.

• Periodical: Materials Science Forum (Volumes 825-826)
• Pages: 677-684
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.825-826.677
• Online since: July 2015
• Authors: Rotraud Freytag*, José Antonio Pérez Gil, Reinhard Forstner
• Keywords: Amorphous Polymers, Injection Molding, pvT Behavior, Semi-Crystalline Polymers, Simulation, Specific Volume

References

[1] G. Menges, P. Thienel, Kunststoffe 65 (1975) 696-699.

[2] M.H.E. van der Beek, Specific volume of polymers: influence of the thermomechanical history, ISBN: 90-386-2567-7, (2005).

[3] R. Forstner, G.W.M. Peters, H.E.H. Meijer, International Polymer Processing XXXIV 2 (2009) 114-121.

[4] J. Wang, PVT Properties of Polymers for Injection Molding, Some Critical Issues for Injection Molding, ISBN: 978-953-51-0298-7, (2012).

DOI: 10.5772/35212