Destruction Patterns of X70 Steel Sample, Possessing Cracks of Corrosion-Mechanical Origin, under Cyclic Loading

Abstract:

Most of the structures, parts of machines in the process of operation are subjected to the action of cyclically changing loads, such changes can be judged by the fatigue of the metal. In addition to the influence of mechanical stresses during the service, corrosive environment affects metal structures, machine parts, which leads to the process of gradual accumulation of damage. Corrosive media leads to a decrease in durability. The paper presents results of fatigue tests on a sample of steel X70, selected from the focal zone of destruction of the main gas pipeline. The sample under investigation had numerous cracks typical for corrosion-mechanical destruction. It is shown that with an increase in the number of loading cycles, the electrode potential of the metal decreases, which leads to a decrease in its thermodynamic stability. With the growth of the crack, there is a decrease in the potential, which is not compensated by the relaxation processes. Results of the regression analysis showed that the correlation coefficient is r = 0.99, using the three-parameter logarithmic function.

• Periodical: Materials Science Forum (Volume 946)
• Pages: 20-24
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.946.20
• Online since: February 2019
• Authors: O.A. Nasibullina*, A.G. Gareev
• Keywords: Correlation Coefficient, Cyclic Loading of Structural Elements, Main Gas Pipeline, Stress-Crack Corrosion, Thermodynamic Stability of Steel

References

[1] A.G. Gareev, R.G. Rizvanov, O.A. Nasibullina, Corrosion and protection of metals in the oil and gas industry, Gilem, Ufa, (2016).

[2] A.G. Gareev, O.A. Nasibullina, R.G. Rizvanov, Investigation of hydrogen metal embrittlement, destructive metalwork, Problems of gathering, treatment and transportation of oil and oil products. 107 №1 (2017) 107-115.

[3] I.G. Abdullin, A.G. Gareev, Corrosion fatigue durability of pipe steel in carbonate-bicarbonate media, Fiziko-Khimicheskaya Mekhanika Materialov. 29 № 5 (1993) 97-98.

DOI: 10.1007/bf00558780

[4] A.S. Tyusenkov, Chemical resistance of steel 13CrV, Steel. 2 (2016) 53-57.

[5] O.A. Nasibullina, A.G. Gareev, R.G. Rizvanov, Investigation of the Hydrogen Stratification of the Metal of the Active Gas Pipeline, Solid State Phenomena, 284(2018) 1302-1306.

DOI: 10.4028/www.scientific.net/ssp.284.1302

[6] A.S. Tyusenkov, A.V. Rubtsov, R.R. Tlyasheva, Heat Resistance of Certain Structural Steels, Solid State Phenomena. 265 (2017) 868-872.

DOI: 10.4028/www.scientific.net/ssp.265.868

[7] O.A. Nasibullina, A.G. Gareev, R.G. Rizvanov Investigation of the Hydrogen Stratification of the Metal of the Active Gas Pipeline, Solid State Phenomena, 284 (2018) 1302-1306.

DOI: 10.4028/www.scientific.net/ssp.284.1302

[8] R.G. Rizvanov, R.G. Abdeev, N.L. Matveev, R.G. Ryskulov, A.I. Shenknekht A.F. Insafutdinov, Effect of the geometry of the shell/elliptical-bottom contact zone on the stress state of pressure vessels, Chemical and Petroleum Engineering. 36 (2000) 3.

DOI: 10.1007/bf02463460

[9] M.G. Bashirov, M.I. Kuzeev, I.R. Kuzeev, A.I. Yunkin, Electromagnetic method of diagnosis in problems of operation safety assurance and evaluating the service life of equipment at petrochemical and petroleum-processing plants, Bezopastnost' Truda v Promyshlennosti, 2 (2004) 49-54.

[10] I.R. Kuzeev, I.G. Ibragimov, M.I. Bayazitov, S.N. Davydov, I.R. Khairudinov, Steel corrosion prevention in coking residual petroleum stocks, Chem. and Technology of Fuels and Oils. 22 № 3 (1986) 111-113.

DOI: 10.1007/bf00726125

[11] A.G. Gareev, O.A. Nasibullina, R.G. Rizvanov, Study of corrosion cracking of main gas and oil pipelines, Oil and gas business: electronic scientific journal, 6 (2012) 126-146.

[12] A.S. Tyusenkov, S.E. Cherepashkin, Scale Inhibitor for Boiler Water Systems, Russian J. of Applied Chem. 87 № 9 (2014) 1240-1245.

DOI: 10.1134/s1070427214090080

[13] E.A. Filimonov, I.R. Kuzeev, Evaluation of stressed state of coker reactor shell with plastic deformation, Chemistry and Technology of Fuels and Oils, 22 №7 (1986) 352-355.

DOI: 10.1007/bf00730524

[14] N.K. Tsenev, I.R. Kuzeev, V.A. Baryshev, A.M. Gallyamov, B.E. Selsky, The influence of dislocation structure and intergranular boundaries on the character of fracture in the low carbon steel St3, Materials Science Forum, 207-209 (PART 2) (1996), 685-688.

DOI: 10.4028/www.scientific.net/msf.207-209.685

[15] I.R. Kuzeev, G.E. Zakirnichnyi, L.F. Zakirova, Change in mechanical properties of two-layer steel 16GS + 08Kh13 in the process of long-term operation, Metal Science and Heat Treatment, 51 (9-10) (2009), 450-453.

DOI: 10.1007/s11041-010-9191-z