Research on Corrosive Wear Properties of Super High Chromium Cast Iron

Abstract:

National standard high chromium cast iron contains 26% chromium by weight (Cr26). A new type of Super High Chromium Cast Iron (SHCCI) has been developed with chromium content of about 37% by weight. This paper examines the microstructure of SHCCI using SEM and XRD. The hardness and toughness of SHCCI was studied and the corrosive wear properties of SHCCI were also examined using an MCF-30 type erosion abrasion tester under H3PO4 media. The results show that, the microstructure of SHCCI is composed of M7C3 and M23C6 carbides, martensite matrix and residual austenite matrix. With proportionately greater carbon content, the hardness of SHCCI will first increase and then decrease, while the toughness and corrosive wear properties will decrease gradually SHCCI’s corrosive wear performance was significantly better than that of Cr26 cast iron. The maximum wear capacity of SHCCI is three times higher than that of Cr26 cast iron.

• Periodical: Advanced Materials Research (Volume 1094)
• Pages: 292-295
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.1094.292
• Online since: March 2015
• Authors: Bao Yuan Li*, Hong Bo Guo, Liu Jie Xu, Shi Zhong Wei, Kun Wu, Xiong Yang, Guang Du
• Keywords: Corrosive Wear, Microstructure, Super High Chromium Cast Iron (SHCCI)

References

[1] Le Lin: China's phosphate and compound fertilizer industry after WTO entry for one year. The Tenth Annual Meeting Proceedings of National Chemical sulfuric acid and phosphate fertilizer Design Technology Center [M]. Nanjing. 2003. 5: 1-2, In Chinese.

[2] Lianping Cheng, Qilong Yong and Guoliang Zhang: Journal of Kunming University of Science and Technology (Science and Technology Edition). 2002. 27 (2): 36-39, 42, In Chinese.

[3] Llewellyn R. J, Yick S. K and Dolman K. F: Wear. 2004. 256(6): 592-599.

[4] Shangang Zhang, Wei Huang and Zhanjun Zhao, etal.: Foundry Technology. 2004. 25 (6): 408-410, In Chinese.

[5] Daiying Guo, Jianwei Fan and Xiaohui Zhi: China Foundry Machinery & Technology. 2009. (4): 24-26, In Chinese.

[6] Nong Wan, Qiwu Wei, Jianfang Zheng, etc.: Heat Treatment of Metals. 2007. 32(S1): 252-254, In Chinese.

[7] Youping Ma, Xiulan Li and Yugao Liu et al.: Bulletin of Materials Science, 2013, Vol. 36 (5), pp.839-844.

[8] Hanguang Fu, Xiaojun Wu and Xueyi Li, et al.: Materials Engineering and Performance, 2009, Vol. 18 (8), pp.1109-1115.

[9] Yuncheng Hou, You Wang and Zhaoyi Pan, et al.: Rare Earths, 2012, Vol. 30 (3), pp.283-288.

[10] Liu Jie Xu, Bao Yuan Li and An Heng Si et al.: Advanced Materials Research, 2014, Vol. 3226 (941), pp.1367-1371.