Preparation of Cobalt and Copper Superfine Composite Oxides and Magnetic Property

Abstract:

A series of Co–Cu composite oxides with different susceptibility were prepared by a microemulsion method. XRD, TEM, EDS，FT-IR spectra , TG-DSC and magnetic balance were used to characterize the structure , thermostability and susceptibility of the composite oxides. The results indicate that sintering temperature has an apparent effect on the formation of the spinel structure, As the composite powders are annealed at 500 °C,the Co–Cu composite oxide was CuO 、CoO、 Cu2CoO3 and Co3O4 , but the susceptibilities of Co-Cu composite were found decreased with the annealing, and particle sizes of the composite oxides were increased in the beginning, and then became lower with the annealing .The element Co is found when the calcinations temperature is lower than 300°C.particle sizes of the composite oxides were increased at beginning, then reduced, and increased when over 500°C

• Periodical: Advanced Materials Research (Volumes 150-151)
• Pages: 687-692
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.150-151.687
• Online since: October 2010
• Authors: Wei Zhang, Chao Ping Zhang, De Jun Shen
• Keywords: CoCu, Composite Oxide, Microemulsion, Susceptibility, Thermostability

References

[1] Xiao-yuan Jiang, Ren-Xian Zhou, ping Pan et al, Appl. Catal. A: General, 150: 131- 141(1997).

[2] C. A. Q uerini, L. M. Cornaglia,M. A. Ulla, et al, Appl. Catal. B: Environmental, 20: 165-177(1999).

[3] D. Stoyanova, M. Ch ristova, P. D imitrova, et al, Appl. Catal. B: Environmental, 17: 233- 244(1998).

[4] Wu Y, Gao L Zh , Yu Z L. Preparation， Acta Chim Sin , 55 (1) : 56-63 (1997).

[5] J. F. Bringley B. A. Scott S. J. La Placa et al Nature, 347(2690), 263 (1990).

[6] Taylor, R.C. Plechaty, M.M.; Beach, D.B. et al, Comparison of the oxygen evolution upon acid dissolution of Ba0. 6K0. 4BiO3, with the copper-based oxides LaCuO3 and La1. 85Sr0. 15CuO4, Physica C: Superconductivity and its Applications, 1990, 169(1-2), pp.35-38.

DOI: 10.1016/0921-4534(90)90285-m

[7] Wang YZ, Zhao YX, Gao CG, Liu DS ，Catal Lett， 116（3-4）: 136-142 (2007).

[8] Pollard M J, Weinstock B A, Bitterwolf T E et al， J. Catal. 254(2): 218-225(2008).

[9] Wang CB, Tang CW, Gau SJ, Chien SH， Catal. Lett，101（1-2）59-63 (2005).

[10] Zavyalova U, Nigrovski B, Pollok K, Langenhorst F, Mu¨ler B, Scholz P, Ondruschka B, Appl. Catal. B 83(3-4): 221-228(2008).

DOI: 10.1016/j.apcatb.2008.02.015

[11] Nachal Devi Subramanian, G. Balaji, Challa S.S.R. Kumar and James J. Spivey, Catal. Today, 147(2), 100-106(2009).

[12] S. V. Kolotilov, K. S. Gavrilenko, M. R. Kantserova, A. V. Yakovenko, N. N. Stepanenko, N. V. Kas'yan, and A. V. Shvets, Theor. Experim. Chem., 41(6), 544-547(2005).

[13] Aitelhadjali, Z.   Benbrahim, N.   Kadri, A.   Dahmane, Y.   Benfedda, B.   Voiron, J.   Lienard, A.,  Co-Cu granular alloys prepared by electrodeposition, Microelectronics, 2004, ICM 2004 Proceedings. The 16th International Conference on, Publication Date: 6-8 Dec. 2004 On page(s): 668 – 671.

DOI: 10.1109/icm.2004.1434754

[14] Dongdong Gu and Yifu Shen, Appl Surf Sci . 254(13), 3971-3978(2008).

[15] Ming Wen, Qiu-Yan Liu, Ya-Fen Wang, Yuan-Zheng Zhu and Qing-Sheng Wu, Colloids and Surfaces A: Physicochemical and Enginee. Aspects, 318 (1-3), 238-244(2008).

[16] Z.Q. Yang, C.Y. You and L.L. He, J. Alloys and Compounds 423（1-2），128-131(2006).

[17] L.M. García, F. Bartolomé, J. Bartolomé, F. Luis, F. Petroff, C. Deranlot, F. Wilhelm, A. Rogalev, P. Bencok and N.B. Brookes，J. Magn. Magn. Mater, 316（2）, e23-e26(2007).

DOI: 10.1016/j.jmmm.2007.02.016

[18] Yaoshun Jia, Helin Niu, Mingzai Wu, Min Ning, Hongfei Zhu and Qianwang Chen, Mater. Research . Bull. 40(9), 1623-1629(2005).

[19] C. de Julián Fernández, G. Mattei, C. Maurizio, E. Cattaruzza, S. Padovani, G. Battaglin, F. Gonella, F. D'Acapito and P. Mazzoldi, J. Magn. Magn. Mater, 290-291, Part 1, 187-190(2005).

DOI: 10.1016/j.jmmm.2004.11.178

[20] Sreekumar K, Mathew T, Rajagopal R, Vetrivel R, Rao B S, Catal. Lett, 65(1-3): 99-105 (2000).

[21] Zarate RA, Hevia F, Fuentes S, Fuenzalida VM, Zu´n˜iga A, J Solid State Chem , 180(4): 1464-1469( (2007).

[22] Zavyalova U, Nigrovski B, Pollok K, Langenhorst F, Mu¨ler B, Scholz P, Ondruschka B . Appl. Catal. B 83(3-4): 221-228(2008).

DOI: 10.1016/j.apcatb.2008.02.015

[23] Cesar DV, Pere´z CA, Schmal M, Salim VMM, Appl Surf Sci 157(3): 159-166(2000).

[24] Wang X，Lee B I，Hu M，et al. Mechanism of nanocrystalline BaTiO3 particle formation by hydrothermal refluxing synthesis., J Mater Sci-Mater Electron，14(8)：495-500. (2003).

[25] Li, Xingguo ，Takahashi, Seiki ，Synthesis and magnetic properties of Fe-Co-Ni nanoparticles by hydrogen plasma-metal reaction，J. Magn. Magn. Mater, 214(3), 195-203( 2000).

DOI: 10.1016/s0304-8853(00)00081-0

[26] KOda Kiichi Yoshio, Tetsuo Oda Kohei, PREPARATION OF CO-N FILMS BY RF-SPUTTERING, J. Mater. Sci., 22(8), 2729-2733(1987).

DOI: 10.1007/bf01086464

[27] A. F. WELLS, Structural Inorganic Chemistry, ， Clarendon Press, Oxford, (1975), p.1051.