Study on Control Technology of Transverse Corner Cracks on CC Slab for Automobile Frame Steel Plate

Abstract:

Article Preview

There were serious transverse corner cracks on continuous casting slab of automobile frame steel plate in Panzhihua Steel before, and study on the control of transverse corner cracks had been carried out. Some effective countermeasures are put forward, such as the optimization of ratio of heat flux density on narrow side and broad side of casting slab (RHFD) and mold powder, as well as the stabilization of casting speed and working condition of caster. Industrial test shows that the transverse corner cracks on continuous casting slab have been significantly reduced, and the lines and peeling defects on hot rolled sheet have been eliminated due to the transverse corner cracks.

Info:

Periodical:

Advanced Materials Research (Volumes 295-297)

Edited by:

Pengcheng Wang, Liqun Ai, Yungang Li, Xiaoming Sang and Jinglong Bu

Pages:

636-640

DOI:

10.4028/www.scientific.net/AMR.295-297.636

Citation:

H. Pan et al., "Study on Control Technology of Transverse Corner Cracks on CC Slab for Automobile Frame Steel Plate", Advanced Materials Research, Vols. 295-297, pp. 636-640, 2011

Online since:

July 2011

Export:

Price:

$35.00

[1] Cai Kaike. Quality control for continuous casting slab [M]. Beijing: Metallurgical Industry Press, 2010: 216-217.

[2] Chang Guihua, Lv Zhisheng, Cao Dong, etl. Factors leading to transverse crack at corner of continuous casting micro-alloying slab [J]. Angang Technology, 2006(6): 25-28.

[3] Mintz B. The influence of composition on the hot ductility of steals and to the problem of transverse cracking [J]. ISIJ Int, 1999, 39(9): 8.

[4] Hwang B, Lee H S, Kim Y G, et al. Analysis and prevention of side cracking phenomenon occurring during hot rolling of thick low carbon steel plates [J]. Mater Sci Eng A, 2005, 402(8): 177.

DOI: 10.1016/j.msea.2005.04.045

[5] Dobrovska J, Stransky K, Kavicka F, et al. Analysis of a transversal crack in a steel slab [J]. Mater Sci Forum, 2008, 567-568: 105.

DOI: 10.4028/www.scientific.net/msf.567-568.105

In order to see related information, you need to Login.