The Effect of CaO and MgO on Physical Properties of MgO-CaO-B2O3-Al2O3-SiO2 Glasses with Composition Close to the E-Glass Fibers

J. Kraxner; R. Klement; Mária Chromčíková; Marek Liška

doi:10.4028/www.scientific.net/AMR.39-40.81

Paper Titles

Structural Changes in Alkali Depleted Alkali-Silicate Glass – MD Study
p.65

Structural Model of K₂O-GeO₂-P₂O₅Glasses Based on Diffraction Results
p.69

Glass Formation and Structure of the Glasses in the MoO₃-Nd₂O₃-Bi₂O₃ System
p.73

Silicon Oxycarbide Glasses from Gel Hybrid Structures
p.77

The Effect of CaO and MgO on Physical Properties of MgO-CaO-B₂O₃-Al₂O₃-SiO₂ Glasses with Composition Close to the E-Glass Fibers
p.81

First Principles Molecular Simulations of Soda-Lime-Silica Glass
p.85

Volumetric Changes Between Different Conformations of Two SiOH Groups in SiO₂ Glass
p.89

The Yttria-Alumina Glasses - MD and TD Models
p.93

Zinc Borophosphate Glasses Doped with Molybdenum Oxide
p.97

HomeAdvanced Materials ResearchAdvanced Materials Research Vols. 39-40The Effect of CaO and MgO on Physical Properties...

The Effect of CaO and MgO on Physical Properties of MgO-CaO-B₂O₃-Al₂O₃-SiO₂ Glasses with Composition Close to the E-Glass Fibers

Abstract:

High temperature viscosity and density of glass melts, glass transition temperature, and thermal expansion coefficient of glasses from the system MgO-CaO-B2O3-Al2O3-SiO2 with composition close to the E-glass were measured and interpreted with respect to the effect of CaO and MgO content on their physical properties. The Andrade model was applied for description of the temperature dependence of the glass viscosity within studied temperature range. The regression formaulae describing the compositional dependence of the viscosity points T2 = T( η = 100 dPa.s), T3 = T( η = 1000 dPa.s), the glass transition temperature, Tg, thermal expansion coefficient of glass, αg , and of the viscous flow activation energy, Ea, were proposed.