Oxidation Resistance of Al-Rich Aluminide Coating on TiAl Based Alloy by Thermal Spray and Diffusion Treatment

Abstract:

Al-rich aluminide coating on Ti-49.1at%Al alloys has been performed by two-step process of thermal aluminum spray and diffusion treatment. Effect of the diffusion time on the oxidation resistance, and the change of microstructures in the coating during the oxidation test in air at 900°C for 100 h were investigated. In the aluminized coating before the oxidation tests, formations of TiAl₃ on the outer layer and an intermediate layer consisting of Ti₂Al₅, TiAl₂, and Al-rich TiAl were observed. The intermediate layer developed by the diffusion treatment for 3600s. In the oxidation test over 50 h, the specimen diffusion treated for 3600 s exhibited the lower oxidation rate than that diffusion treated for 900 s. Multi-oxide scales of TiO₂ and Al₂O₃ were observed on the both surfaces of aluminized specimens. Large TiO₂ particles were observed on the specimen of t_D = 900 s. It was found that the TiAl₂ layer developed during the oxidized specimen, while the thicknesses of Al-rich TiAl and TiAl₃ layer decreased by the growth of TiAl₂.

• Periodical: Advanced Materials Research (Volume 409)
• Pages: 820-825
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.409.820
• Online since: November 2011
• Authors: Takahiro Yagi, Tomohiro Sasaki, Takehiko Watanabe, Atsushi Yanagisawa
• Keywords: Aluminizing, Diffusion, Intermetallic, Oxidation Resistance, Surface Coating, TiAl

References

[1] F. Appel, M. Oehring in : Titanium and titanium alloys: fundamentals and applications edited by C. Leyens, M. Peters, chapter, 4, Wiley-VCH (2003).

[2] T. Sasaki, T. Yagi, and T. Watabe: Mater. Sci. Forum Vol. 654-6560 (2010), p.1884.