Failure Analysis on Fracture of a 3-1/2″ P110SS Tubing

Yan Han; Xue Hui Zhao; Juantao Zhang; Rui Cai; Guan Fa Lin

doi:10.4028/www.scientific.net/AMR.524-527.1412

Paper Titles

Experiment Research of Flooding Efficiency on Alternative Injection of Low-Tension System and Foam System
p.1389

Experimental Research of the Acoustic Emission (AE) Characteristics during the Tensile Process of the Blowout Preventer Shell Material
p.1395

Experimental Study on Ball Sealer Diversion for Lateral Well
p.1399

Experimental Study on the Scaling of Water Injection Wells in Xianhe
p.1408

Failure Analysis on Fracture of a 3-1/2″ P110SS Tubing
p.1412

Flow Mathematic Model and Exact Solution of Swabbing Wells’ Fluid Level Build up
p.1418

Full Transient Features of Heat Transfer and Sensitivities on Deep Water Wells
p.1423

Generational Technology of Computational Grid in Porous Media Based on Digital Image
p.1429

Gudao Oilfield Fault Seal Ability Research and Development of Oil and Gas Application
p.1435

HomeAdvanced Materials ResearchAdvanced Materials Research Vols. 524-527Failure Analysis on Fracture of a 3-1/2″ P110SS...

Failure Analysis on Fracture of a 3-1/2″ P110SS Tubing

Abstract:

The tubing, as a key ingredient in the well development, worked always under very complex stress and corrosion conditions, the failure of the tubing could cause huge losses. In this paper, a fractured 3-1/2″ P110SS tubing was analyzed through physical and chemical properties testing, SEM, EDS, and XRD method. The results showed that the failure of the tubing was belong to hydrogen sulfide stress corrosion cracking. The tubing material could not pass the SSC test, it was inappropriate to use in well contained high hydrogen sulfide.

You might also be interested in these eBooks

Natural Resources and Sustainable Development II

View Preview

Info:

Periodical:

Advanced Materials Research (Volumes 524-527)

Pages:

1412-1417

DOI:

https://doi.org/10.4028/www.scientific.net/AMR.524-527.1412

Citation:

Cite this paper

Online since:

May 2012

Authors:

Yan Han, Xue Hui Zhao, Juantao Zhang, Rui Cai, Guan Fa Lin

Keywords:

Failure Analysis, Fracture, Hydrogen Sulfide Stress Corrosion Cracking

Export:

RIS, BibTeX

Price:

Permissions CCC:

Request Permissions

Permissions PLS:

Request Permissions

Сopyright:

Citation:

References

[1] Q/SY-TGRC2-2009, Recommended practice for tubing and casing of carbon and low alloy steels for use in H2S-containing environments.2010.CNPC Tubuler goods reaserch institute.

Google Scholar

[2] API RP 5C5, Recommended Practice on Procedures for Testing Casing and Tubing Connections. Third edition, 2003. Washington DC: API.

Google Scholar

[3] Jun Hu,Fei Liu,Guangxu Cheng,et al: Annals of Nuclear Energy, 38(2011), p.1901.

Google Scholar

[4] G.Pantazopoulos,A.Vazdirvanidis,G.Tsinopoulos:Engineering Failure Analysis 18(2011), p.650.

Google Scholar

[5] Sun Zhi,Jiang Li,Ying Pengzhan,in:Failure Analysis.China machine press,Bei Jing,2009, p.125.

Google Scholar