Oxidation Behavior of Ternary Co-10Cr-5Al Alloys at 700 and 800°C

Abstract:

The kinetics and products of oxidation of ternary Co-10Cr-5Al alloys in 1 atm of pure O2 at 700 and 800 oC were investigated. Oxidation of the alloys approximately obeyed the parabolic rate law. The scale formed at 700 oC was composed of an outer CoO layer and an inner complex layer rich in Al2O3 and Cr2O3 which were intermingled with spinel Co(Cr, Al)2O4. There was no internal oxidation zone beneath the scale. However, as shown by Fig. 3. b, internal oxidation zone of Al or even Cr was obviously present beneath the scale formed at 800 oC, though the scale was of a similar microstructure with that at 700 oC.

• Periodical: Advanced Materials Research (Volumes 560-561)
• Pages: 1068-1071
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.560-561.1068
• Online since: August 2012
• Authors: Jun Huai Xiang, Hong Hua Zhang, Ling Yun Bai, Yi Li
• Keywords: Co-10Cr-5Al, High-Temperature, Isothermal Oxidation, Microstructure

References

[1] J. Sato, T. Omori, K. Oikawa, I. Ohnuma, R. Kainuma and K. Ishida: Science. Vol. 312 (2006), p.90.

DOI: 10.1126/science.1121738

[2] G.W. Goward: Surf. Coat. techno. Vol. 108-109 (1998), p.73.

[3] J.W. Lee, Y.C. Kuo: Surf. Coat. Technol. Vol. 200 (2005), p.1225.

[4] K. Zhang, Q.M. Wang, C. Sun and F.H. Wang: Corros. Sci. Vol. 50 (2008), p.1707.

[5] J.H. Xiang, Y. Niu and F. Gesmundo: Corros. Sci. Vol. 47 (2005), p.1493.

[6] W. Wang, P. Yu, F. H. Wang and S. L. Zhu: Surf. Coat. Technol. Vol. 201 (2007), p.7425.

[7] C.S. Tedmon: J. Electrochem. Soc. Vol. 113 (1996), p.766.

[8] G.N. Irving, J. Stringer and D.P. Whittle: Oxid. Met. Vol. 9 (1975), p.427.

[9] K. Przbylski, D. Szwagierczak: Oxid. Met. Vol. 17 (1982), p.267.

[10] F.H. Wang, H.Y. Lou and W. Wu: Vacuum Vol. 43 (1992), p.749.

[11] G. R. Wallwork and A. Z. Hed: Oxid. Met. Vol. 3 (1971), p.213.

[12] F.H. Stott, G.C. Wood and M.G. Hobby: Oxid. Met. Vol. 3 (1971), p.103.