Improving the Properties of Magnetic Bearing Shaft Material by HVOF Coating of WC-Metal Powder and Laser Heat Treatment

Abstract:

Abstract. Micron-sized WC-metal (WC-0.6%C-21%Cr-6%Ni) powder was coated onto the substrate of magnetic bearing shaft material Inconel718 (substrate or In718) using JK3500 HVOF thermal sprayer for the improvement of the surface properties of the substrate. The optimal coating process for the highest surface hardness was obtained using the Taguchi experimental program. The coating was laser heat-treated (LH) by CO2(g) laser for further improvement of the properties. During the thermal spraying, a small portion of metal carbides of powder decomposed to W2C, metals and free carbon. The free carbon reacted with excessively sprayed oxygen, and formed carbon oxide gases, forming porous coating. By laser-heating, porosity decreased and the porous strips at the interface of coating and substrate (coat/sub) compacted. At the interface, the precipitated graphite concentration decreased and the metal elements diffused from both the coating and substrate increased, enhancing the functions as buffer zone and increasing adhesion of coating. The surface hardness of substrate increased by coating and further increased by laser-heating from 410±30 Hv to 983±101 Hv and 1425±94 Hv respectively. Porosity of coating decreased by laser-heating from 2.6±0.4% to 0.35±0.06%, and coating thickness shrank from 280㎛ to 200㎛. Friction coefficients of substrate decreased from 0.52±0.02 to 0.36±0.04 by coating, because the free carbon formed by decomposition of WC to W2C functioned as a solid lubricant. By increasing sliding surface temperature from 25°C to 450°C, the friction coefficients of substrate and coating were decreased from 0.52±0.02 to 0.31±0.02 and from 0.36±0.04 to 0.23±0.04 respectively, because of easy formation of free carbon and metal oxides which functioned as solid lubricants. Wear depth of surface was decreased by coating and by LH coating from 55µm to 32 µm and to 12 µm respectively. HVOF coating of WC-metal powder on In718 surface and laser heat-treatment of the coating are highly recommended for the improvement of the properties of magnetic bearing shaft.

• Periodical: Advanced Materials Research (Volumes 560-561)
• Pages: 1052-1058
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.560-561.1052
• Online since: August 2012
• Authors: T.Y. Cho, Y.K. Joo, J. H. Yoon, H. G. Chun, S.H. Zhang
• Keywords: Hardness, HVOF Coating, Porosity, Surface Property

References

[1] J. R. Davis, Handbook of Thermal Spray Technology, 1 (ASM International, USA, 2004). pp.1-150.

[2] B.D. Sartwell, K. Legg, B. Bodger, AESF/EPA Conference for Environmental Excellence, 231, 1 (1999), pp.1-120.

[3] T. Y. Cho, J. H. Yoon, K. S. Kim, W. Fang, Y. K. Joo, K. O. Song. S. J. Youn, S. Y. Hwang and H. G. Chun, J. Advanced Materials Research 26-28, 1325 (2007).

[4] T. Y. Cho, J. H. Yoon, K. S. Kim, S. J. Youn, N. K. Baek, B. C. Park, S. Y. Hwang and H. G. Chun, Kor. Soc., Machine Tool Engineers, 15-6, 32 (2006).

[5] T.Y. Cho, J.H. Yoon, S.K. Hur, H.G. Chun, Shi-hong Zhang, Surface Modification by HVOF Coating of Micron-sized WC-metal Powder and Laser-heating of the Coating, Materials Science Forum Vol. 686 (2011) pp.654-660.

DOI: 10.4028/www.scientific.net/msf.686.654

[6] Tong Yul Cho, Yoon Gyo Jung, Jae Hong Yoon, Yun Kon Joo, Hui Gon Chun, A Study on the Surface Properties and Wear Behavior of HVOF Thermal Spray Coating of Micron-sized Cobalt Alloy Powder", Proceedings of the First Int, l Conference on Manufacturing Process Technology (ICMPT-01 2011), Gyungsang National University, Jinju, Korea, May 27-30, (2011).

DOI: 10.4028/www.scientific.net/amr.75.19

[7] T.Y. Cho, J.H. Yoon, Y.K. Joo, S.H. Zhang, J.Y. Cho, J.H. Kang, H.G. Chun, S.C. Kwon, Ming-Xi Li, Improving the surface properties of Inconel 718 by applying a CO2 laser heat treatment to a High- velocity Oxy-fuel coating of WC-CrCo powder, Surface Review and Letters, Vol. 17, Nos. 1 & 2 (2010).

DOI: 10.1142/s0218625x10013849

[8] T. Y. Cho, J. H. Yoon, K. S. Kim, S. J. Youn, K. O. Song, H. G. Chun and S. Y. Hwang, J. Kor. Inst., Surf. Eng., 39-5, 240 (2006).

[9] T. Y. Cho, J. H. Yoon, K. S. Kim, N. K. Baek, K. O. Song, S. J. Youn, S. Y. Hwang and H. G. Chun, J. Kor. Inst., Surf. Eng., 39-6, 295 (2006).

[10] T. Y. Cho, J. H. Yoon, K. S. Kim, W. Fang, Y. K. Joo, K. O. Song, S. J. Youn, S. Y. Hwang and H. G. Chun, J. Kor. Inst., Surf. Eng., 40-4, 170 (2007).

[11] T. Y. Cho, J. H. Yoon, K. S. Kim, S. J. Youn, K. O. Song, H. G. Chun and S. Y. Hwang, Corrosion Science and Technology 6-4, 159 (2007).

[12] J. E. Cho, S. Y. Hwang and K. Y. Kim, Surface & Coating Technology 200, 2653 (2004).

[13] P. Chivavibaul, M. Watanabe, S. Kuroda and K. Shinoda, Surf. & Coat. Technology 202, 509 (2004).

[14] T. B. Massalski, H. Baker, W. W. Scot, Binary Alloy Phase Diagram, Am. Soc. for Metals, 1, 600 (1986).

[15] U.T. Kim, D.W. Park, J.S. Kim, Y.S. Kwon, H.S. Kwon, and B.R. Baek, J. Korea Powder Metall. Inst. 10 (2003), p.176.