Fabrication of Super-Hydrophobic Film on Tinplate’s Surface by a Simple Casting Method in Material Engineering and its Application

Abstract:

Article Preview

A simple, cheap and environmental double thin super-hydrophobic composite film was prepared on the surface of tinplate by a simple casting method. The contact angle and sliding angle were measured by an optical contact angle meter. And the major factors that influenced the super-hydrophobic effect of the composite film were studied in our work. The results showed that when the melting temperature was 120°C, the weight radio of PP and PP-g-MAH was 1:4, the drying time was 24h, the dosage of ethanol was 0.4ml, the composite film showed a satisfactory super-hydrophobicity and its water contact angles reached a maximum value of 156.6° while the sliding angle reached a minimum value of 2°. Because of anti-oxidation, moisture-proof and anticorrosion performance of super-hydrophobic tinplate, it has potential practical applications in packaging material engineering.

Info:

Periodical:

Edited by:

B. Xu and H.Y. Li

Pages:

374-378

Citation:

Q. L. Liu et al., "Fabrication of Super-Hydrophobic Film on Tinplate’s Surface by a Simple Casting Method in Material Engineering and its Application", Advanced Materials Research, Vol. 583, pp. 374-378, 2012

Online since:

October 2012

Export:

Price:

$38.00

[1] A. Chundera, K. Etcheverryb, G. Londec, H.J. Chob, L. Zhaia: Colloids Surfaces A: Physicochem. Eng. Aspects Vol. 333 (2009) p.187.

[2] S. Li, H. Xie, S. Zhang, X. Wang: Chem. Commun. (2007) p.4857.

[3] I.A. Larmour, G.C. Saunders, S.E.J. Bell: New J. Chem. Vol. 32 (2008) p.1215.

[4] N.J. Shirtcliffe, G. McHale, M.I. Newton, G. Chabrol, C.C. Paul: Adv. Mater. Vol. 16 (2004) p. (1929).

[5] N. Zhao, J. Xu, Q.D. Xie, L.H. Weng, X.L. Guo, X.L. Zhang, L.H. Shi: Macromol. Rapid Commun. Vol. 26 (2005) p.1075.

[6] J. Fresnais, J.P. Chapel, F. Poncin-Epaillard: Surface Coat. Technol. Vol. 200 (2006) p.5296.

[7] B.T. Qian, Z.Q. She: Langmuir Vol. 21 (2005) p.9007.

[8] X.D. Wu, L.J. Zheng, D. Wu: Langmuir Vol. 21 (2005) p.2665.

[9] S.M. Li, Y.G. Wang, J.H. Liu, W. Wei: Journal of Chemical Physics Vol. 23(2007) p.1631.

[10] Liu Y, Chen X, Xin J H. Nanotechnology Vol. 17 (2006) p.3259.