Preparation and Properties of Optically Transparent Chitin Nanofibers Sheet by Different Simple Mechanical Methods

Abstract:

Chitin nanofibers were prepared from commercially available dried chitin powders by different simple mechanical methods under acid conditions after removal of minerals and proteins. The fibrillated chitin samples were observed by FE-SEM and there was a fine network structure formed by chitin nanofibes with a width of approximately 10-50 nm and high aspect ratio. The mechanical treatment under acid conditions was crucial to facilitate the fibrillation of chitin fibers into nanofibers. The high pressure homogenization in combination with grinding was used to obtain the most transparent chitin nanofibers sheet with a transmittance of 88.5% and tensile strength of 82.34MPa, and the sheet even had a Young’s modulus of 6.17GPa. Thus, chitin nanofibers provide excellent potential as reinforcement of transparent flexible composites to improve the properties of nanocomposites.

• Periodical: Advanced Materials Research (Volumes 634-638)
• Pages: 2232-2237
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.634-638.2232
• Online since: January 2013
• Authors: Qin Qin Hu, Da Gang Li, Ai Jun Li, Wen Biao Gu
• Keywords: Chitin Nanofibers, Fibrillation, Mechanical Method, Optical Transparency

References

[1] Gopalan Nair, K.; Dufresne, A. Biomacromolecules 2003, 4, 657–665.

[2] Abe, K.; Iwamoto, S.; Yano, H. Biomacromolecules 2007, 8, 3276–3278.

[3] Raabe, D. et al. Mater. Sci. Eng., A 2006, 421, 143–153.

[4] Md. Iftekhar Shams et al. Soft Matter 2012, 8, 1369-1373.

[5] M. Iftekhar Shams et al. Appl Phys A 2011, 102:325-331.

[6] Chen, P.-Y.; Lin, A. Y.-M.; McKittrick, J.; Meyers, M. A. Acta Biomater 2008, 4, 587–596.

[7] Fan, Y.; Saito, T.; Isogai, A. Biomacromolecules 2008, 9, 192–198.

[8] Shinsuke Ifuku et al. Carbohydrate Polymers 2010, 81, 134-139.

[9] Raabe, D.; Sachs, C.; Romano, P. Acta Mater. 2005, 53, 4281–4292.

[10] M. Wada, Y. Saito, J. Polym. Sci., B, Polym. Phys. 2001, 39, 168–174.