Analyzing and Control of Surface Inclusion Defect of Hot-Rolled Coil

Abstract:

This paper is considering the surface quality control of hot-rolled coil. Through analyzing patterns, distributing-regularities and components of surface defect of low-carbon coil of WISCO, got the conclusion that mould powder entrapment was the key factor that lead the defect’s occurrence. Based on discussing the mechanism of powder entrapment in mould, developed a type of high viscosity powder, optimized flow field of mould through modifying the structure of SEN, and improved other relevant process conditions, the incidence rate of this type of defect was under controlled effectively and the degradation rate of the coil caused by the defect dropped from about 4 percent to less than 0.2 percent at the end.

• Periodical: Advanced Materials Research (Volumes 753-755)
• Pages: 230-235
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.753-755.230
• Online since: August 2013
• Authors: Yin Lan, Yan Feng Wang, Zhi Zheng Yang, Jiang Ping Rao, Xia Hong
• Keywords: Flow Field, Powder Entrapped, Surface Inclusion, Viscosity

References

[1] Qiaotong Lu; Shifu Cheng: Principle and process of continuous casting. Beijing , China, 1994, pp.121-135.

[2] Jinghao Chi; Yongnian Gan: Mould powder of Continuous casting. Shenyang, China, 1993, pp.87-99.

[3] Dengfu Chen; Jianhua Zheng: Key technology for high efficiency continuous casting. Special steel, 2002, 23(5), pp.1-4.