Mathematical Modeling of Decarburization and Oxidation during Reheating Process of SAE1070 Steel Billets

Article Preview

Abstract:

The SAE1070 steel grade, used especially in the automotive industry, has strict specifications and some of them are limits to oxidation and decarburization, which implies carbon loss through a variety of diffusion mechanisms. Temperature, atmospheric oxygen potential, carbon chemical potential gradient and time of high temperature exposure are some of parameters, that influence the extent of decarburization. Oxidation influences decarburization losses, in the metal/oxide interface, and as a result of this interface moves into the sample. During the reheating of billets for hot rolling, measures to contain oxidation to the minimum becomes a priority. In this work, the extent of oxidation and decarburization has been studied in the laboratory under industrial conditions as industrial scale experiments are expensive and not very practical. Mathematical modeling based on the results of laboratory experiments becomes attractive as this can be applied to industrial conditions. Isothermal tests for the evaluation of oxidation and decarburization were conducted in an electric furnace in the temperature range 600°C - 1100°C and time ranging from 2 hours to 48 hours. Decarburization and oxidation were measured by techniques such as weight change ue to removal of scale, micro-hardness testing and optical microscopy. Based on the methodology ,an algorithm has been developed for assessment of oxidation and decarburization occurring in the industrial reheating of billets With minor adjustments, it is shown that, the model can be satisfactorily applied with reasonable accuracy. Keywords: Decarburization, Oxidation , Steel billets , Modeling

You might also be interested in these eBooks

Info:

Periodical:

Pages:

231-236

Citation:

Online since:

December 2013

Export:

Price:

Permissions CCC:

Permissions PLS:

Сopyright:

© 2014 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

[1] N Birks, G. H. Meier and F. S. Pettit, Introduction to the high-temperature oxidation of metals, second edition, Cambridge University Press, (2009).

Google Scholar

[2] N Birks and W. Jackson, Quantitative treatment of simultaneous decarburization and scaling of steel, Journal of Iron and Steel Institute, (1970), 81.

Google Scholar

[3] N. Birks and A. Nichoson, Calculation of decarburization depth in steels reheated under practical conditions, ISI Publication 123, London, (1970), 219.

Google Scholar

[4] A. Yokohama and Y. Nuri, Analysis of decarburization phenomena during heating and rolling of billets, Vol. 8 Sanyo Technical Report (2001) No. 1.

Google Scholar

[5] J. Cermak and L. Kral, Low temperature diffusion of carbon in iron measured by SIMS technique, Roznov pod Radhostem, Czech Republic, EU Metal (2010).

Google Scholar

[6] C. Wells et al. Diffusion coefficient of carbon in austenite, Journal of Metals, Transactions AIME, Vol 188 (1950), 553-560.

Google Scholar

[7] S. W. Mayott, Analysis of the effects of reduced oxygen atmospheres on the depths of decarburization of 300M Alloy steel. 2010. Master of Science thesis, Materials science and engineering faculty of Rensselaer Polytechnic Institute.

Google Scholar

[8] ASTM Standard E1077-01, 2005, Standard test methods for estimating the depth of decarburization of steel specimens, ASTM International, West Conshohocken, PA, 2005, DOI: 10. 1520/E1077-01R05, www. astm. org.

Google Scholar

[9] J. F. Elliot, M. Gleiser, V. Ramakrishna, Thermochemistry for Steelmaking, Addison-Wesley Publishing, (1963).

Google Scholar

[10] L. Suarez, H. Yvan , E. Xavier and C., Rafael, Development of an experimental device to study high temperature oxidation , Oxidation of Metals 2008, Vol 70(1) 1-13.

Google Scholar