Elucidating Corrosion Performance of Weld in CO₂ Corrosion Environment

Abstract:

Weld corrosion is suspected to contribute to localized corrosion failure of pipelines in CO₂ environment. Some studies on the mitigation of the weld corrosion had been focused on weld metal micro-alloying producing cathodic weld metal but with mixed success result. The inconsistent result is due to lack of understanding on the mechanism of weld corrosion in this corrosive CO₂ environment. This paper presents the study of the possibility of weld corrosion from the galvanic and self-corrosion effects of welded low carbon steel ASTM 106 B pipeline in pH 5-CO₂ saturated environment at 25 °C and 60 °C under stagnant condition. The weld region samples were prepared by metallography method to identify the parent metal (PM), heat affected zone (HAZ) and weld metal (WM) microstructures. Galvanic current was measured for each weld region by zero resistance ammeters (ZRA) and self-corrosion rate was measured by electrochemical impedance spectroscopy (EIS). The total corrosion rate was determined from the summation of galvanic corrosion and self-corrosion for all weld regions. From the galvanic current test result, weld metal was found to be anodic for both 25 °C and 60 °C. Weld metal also experienced the highest self-corrosion rate in the range of 40-98% as compared to parent metal and HAZ region for both 25 °C and 60°C. The total corrosion rate was mainly contributed by the self-corrosion rates and the contribution from galvanic corrosion was considered insignificant. Possible preferential weld corrosion can occur on weld metal region due to differential self-corrosion rates of each weld regions.

• Periodical: Advanced Materials Research (Volumes 875-877)
• Pages: 547-553
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.875-877.547
• Online since: February 2014
• Authors: A.A. Ab Rahman, M.C. Ismail
• Keywords: CO₂ Corrosion, Galvanic Corrosion, Preferential Weld Corrosion, Self-Corrosion Rate

References

[1] M. B. Kermani and L. M. Smith, A Working Report on CO2 Corrosion Control in Oil and Gas Production - Design Considerations, The Institute of Materials 1997, pp.4-5, 28-30. 60°C 25°C.

[2] S. Turgoose, J.W. Palmer and G.E. Dicken, Preferential Weld Corrosion if 1% Ni Welds: Effect of Solution Conductivity and Corrosion Inhibitors, 2005 NACE Corrosion Conference, Paper #05275.

[3] C-M Lee, S Bond and P Woollin, Prefential Weld Corrosion: Effects of Weldment Microstructure and Composition, 2005 NACE Corrosion Conference, Paper #05277.

[4] M. W. Joosten, J. Kolts, P. G. Humble, J. H. Kiefer and J. Marlow, Aspects of Selective Weld and HAZ Attack in CO2 Containing Production Environments, 1996 NACE Corrosion Conference, Paper #00079.

[5] Hugo Guajardo-Martinez, Weld Corrosion HSLA-80 Steel, PhD Thesis, Materials Science and Engineering University of Toronto.

[6] K. Alawadhi, M. Robinson, A. Chalmers, and I.G. Winning, Inhibition of Weld Corrosion in Flowing Brines Containing Carbon Dioxide, 2008 NACE Conference, Paper #08622.

[7] I.G. Winning, N. Bretherton, A. McMahon and Derek McNaughtan, Evaluation of weld corrosion behavior and the application of corrosion inhibitors and combined scale/corrosion inhibitors. 2004NACE Conference, Paper #04538.

[8] S. Olsen, B. Sundfaer and J. Enerhaug, Weld Corrosion in C-Steel Pipelines in CO2 Environments – Comparison between Field and Laboratory Data. 1997 NACE Conference, Paper #043.

[9] Egil Gulbrandsen and Arne Dugstad, Corrosion Loop Studies of Preferential Weld Corrosion and Its Inhibition in CO2 Environments, 2005 NACE Conference, Paper #0576.

[10] 2006 ASM International. Corrosion of Weldments. Chapter 1, Basic Understanding of Weld Crrosion. www. asminternational. org.

[11] Weld Features that Differentiate Weld and Plate Corrosion. ASM International. D.L. Olson, A.N. Lasseigne, M. Marya and B. Mishra, Center for Welding, Joining and Coatings Research, The G.S. Ansell Department of Metallurgical and Materials Engineering, Colorado School of Mines, Golden, CO 80401.

DOI: 10.1007/bf02717486

[12] R. Andreassen and J. Enerhaug, On the Effect of Microstructure in CO2 Corrosion of Carbon Steel Welds, Advances in Corrosion Control and Materials in Oil and Gas Production.