Hole Cold Expansion the Fatigue Mitigation Game Changer of the Past 50 Years

Abstract:

Over the past 50 years, mitigating cracks from holes has been a major focus of aerospace research, design, and stress engineers. Technology and design philosophies were developed to focus on predicting and increasing fatigue life of metal aircraft structure. One of the innovations to have the biggest impact to slow or arrest crack growth was to induce beneficial residual stresses around a hole. The zone of residual compressive stresses shields the hole from the effects of cyclic loads. The split sleeve cold expansion method was pioneered in the early 1970s by Boeing and Fatigue Technology. The split sleeve cold expansion process has become the bench mark method in mitigating fatigue cracks and enhancing durability and damage tolerance of aerospace metal structures. This paper will review the history of cold expansion methods and the evolution of this technology to the controlled and widely accepted methods used by industry today.

• Periodical: Advanced Materials Research (Volumes 891-892)
• Pages: 679-684
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.891-892.679
• Online since: March 2014
• Authors: Len Reid
• Keywords: Cold Expansion, Cold Working, Crack Retardation, Damage Tolerance, Fatigue, Residual Stress

References

[1] FTI Process Specification FTI-8101, Cold Expansion of Holes Using the Standard Split Sleeve System and Countersink Cold ExpansionÔ (CsCxÔ)., September 1994 (first issued June 1981).

[2] Champoux, R.L., Fatigue of Aircraft Structures, Fatigue Prevention and Design, Chameleon Press Ltd., London, 1986, p.41 et seq.

[3] Phillips, J.L., Sleeve Coldworking Fastener Holes, Vol. I, 1974, Air Force Materials Laboratory Report AFML-TR-74-10.

[4] Mann, J.Y., et al, Techniques for Increasing Fatigue Life of Thick-Section Aluminum Alloy bolted Joints, Aluminum, Vol. 60, no. 7, July 1984, pp.515-520.

[5] Reid, L.F., Split Sleeve Cold Expansion as a Rework Process for Previously Cold Expanded Holes., International Committee on Aeronautical Fatigue (ICAF) June (1993).

[6] Krasnowski, B.T. et al, Fatigue Strength and Damage Tolerance of Thin-Walled Riveted Structures with Cold-Worked Holes., American Helicopter Society 56th Forum, Virginia Beach FL, May (2000).

[7] Petrak, G.J. and Stewart, R.P., Retardation of Cracks Emanating from Fastener Holes, Engineering Fracture Mechanics, Vol. 6, Pergamon Press, 1974, pp.275-282.

DOI: 10.1016/0013-7944(74)90025-3

[8] Clark, G., Modeling Residual Stresses and Fatigue Crack Growth at Cold Expanded Fastener Holes, Fatigue Fracture of Engineering Materials Structures, Vol. 14, No. 5.

DOI: 10.1111/j.1460-2695.1991.tb00684.x

[9] Rich, D.L. and Impellizzeri, L.F., Fatigue Analysis of Cold-Worked and Interference Fit Fastener Holes, ASTM STP 637, (1977).

DOI: 10.1520/stp27993s

[10] Reid, L.F., et al, The Evaluation of a Modified Stress Intensity Factor for Cold Expanded Holes, International Committee on Aeronautical Fatigue Conference Proceedings, Seattle WA USA, July 12-16, (1999).

[11] Reid, L.F., Restis, J.H., Determining and Attaining Realistic Inspection Thresholds to Meet Durability and Damage Tolerance Requirements, Second Joint NASA/FAA/DoD Conference on Aging Aircraft, August 31 to September 3, 1998, Williamsburg VA.