Monitoring of Tempering Behavior in Fe-C-Mn Alloys by Precise Measurement of Electrical Resistivity

Article Preview

Abstract:

Mechanical properties in metallic materials are generally determined by microstructure, which is controlled by thermo-mechanical treatment in addition to its composition. Tempering is the conventional process of heat-treated steel. Therefore, understanding microstructural change during the process is especially important. As is well known, electrical resistivity measurement gives useful information regarding microstructures and lattice defects. In this technique, average information can be obtained from larger volume of specimens than TEM specimens as 108 times. So the purpose of this study was to monitor electrical resistivity changes related to microstructural changes during tempering in Fe-0.19 C-1.5 Mn, Fe-0.35 C-1.5 Mn alloys. Bar shaped specimens were cut from the sheets of steels. The specimens were heat-treated in austenite region and then quenched with ice-water. Then tempering was cumulatively carried out by direct dipping in a nitrate bath held at 423-673 K. Electrical resistivities at 77 K (in liquid nitrogen) and 300 K were measured in each state by a direct current (DC) four-point method. The resistivities abruptly decreased and then gradually decreased by the tempering. First drop and following decreasing of resistivities are corresponding to vanishing vacancies in martensite and precipitation of carbide, respectively. The organized resistivites by Hollomon-Jaffe parameter showed infections during the carbide precipitation. The points must be related to transition of precipitation mode.

You might also be interested in these eBooks

Info:

Periodical:

Pages:

173-176

Citation:

Online since:

May 2014

Export:

Price:

Permissions CCC:

Permissions PLS:

Сopyright:

© 2014 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

* - Corresponding Author

[1] G.R. Speich, Tempering of low-carbon martensite, Trans. TMS-AIME 242 (1969) 2553-2564.

Google Scholar

[2] S. Komatsu and S. Fujikawa, Electrical resistivity of light metals and alloys-It's measurement, interpretation and application, J. Japan Inst. Light Metals 47 (1997) 170-181.

DOI: 10.2464/jilm.47.170

Google Scholar

[3] J.H. Hollomon and L.D. Jaffe, Time-temperature relations in tempering steel, Trans. Met. Soc. AIME 162 (1945) 223-249.

Google Scholar

[4] S. Murphy and J.H. Wood Head, An investigation of the validity of certain tempering parameter, Metallurgical Transactions 3 (1972) 727-735.

Google Scholar

[5] T. Inoue, A new tempering parameter and its application to the integration of tempering effect of continuous heat cycle, Tetsu-to-Hagané 66 (1980) 1532-1541.

DOI: 10.2355/tetsutohagane1955.66.10_1532

Google Scholar

[6] H. Wagenblast and S. Arajs, Electrical resistivity of iron carbon alloys, J. Appl. Phys. 39 (1968) 5885-5889.

DOI: 10.1063/1.1656083

Google Scholar

[7] L. J. Cuddy, Recovery of point defects in iron after low-temperature deformation, Acta Metallurgica 16 (1968) 23-28.

DOI: 10.1016/0001-6160(68)90067-9

Google Scholar

[8] F.E. Fujita and A.C. Damask, Kinetics of carbon precipitation in irradiated iron-II Electrical resistivity measurement, Acta Metallurgica 12 (1964) 331-339.

DOI: 10.1016/0001-6160(64)90001-x

Google Scholar