Nanostructure of Fe-C Alloys Prepared by Arc Melting in Vacuum

Article Preview

Abstract:

Three different Fe-C alloys were prepared in vacuum using the arc melting method: hypereutectoid (1.4% C), eutectoid (0.76% C) and hypoeutectoid (0.4% C). Unlike commercial steels, which they always contain Mn and other impurities, our samples were prepared by using high quality powders (99.999 wt.%). The samples were heat-treated and then observed with optical and scanning electronic microscopy (Zeiss EVO MA10). Selected samples were tested by microidentation (microhardness test). After isothermal transformation at 350 °C fine bainite nanostructures were observed in the hypoeutectoid sample, the mean size of which was found to be 50 nm. With the eutectoid sample, following different heat treatment procedures different micro-and nanostructures were measured: pearlite lamellar spacing, spheroidized cementite particles, and martensite needles, whose mean size is 145 nm, 290 nm and 200 nm respectively. The nanostructure of hypereutectoid sample after isothermal transformation at 650 °C, reveals the eutectoid and proeutectoid cementite lamellas with a mean spacing of 390 nm. X-ray diffraction pattern of eutectoid sample indicated the existence of cementite (Fe3C) content which is also confirmed by carbon mapping of pearlite colonies performed with Energy Dispersive X-ray Spectroscopy. The Vickers hardness of the samples compares well to the one of corresponding commercial steels.

You might also be interested in these eBooks

Info:

Periodical:

Pages:

218-228

Citation:

Online since:

January 2017

Export:

Price:

Permissions CCC:

Permissions PLS:

Сopyright:

© 2017 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

* - Corresponding Author

[1] R. Schlatter, Melting and Refining Technology of High Temperature Steels and Superalloys - A Review of Recent Process Developments, Superalloy Proceedings of the Second International Conference, Sponsored by Met. Sot. AIME, Battelle, Columbus, Ohio, MCIC-72-10, September 18-20, 1972, pp Al-40.

DOI: 10.7449/1972/superalloys_1972_a-1_a-40

Google Scholar

[2] R. Kiessling, N. Lange, Non-metallic Inclusions in Steel, Parts I–IV, The Institute of Materials, London, (1978).

Google Scholar

[3] R. J. Bowne, A review of the fundamentals of vacuum metallurgy, Vacuum, 21, 13, (1970).

Google Scholar

[4] A. Choudhury, Vacuum Metallurgy, ASM International, Metals Park, OH, (1990).

Google Scholar

[5] J. Deep Singh, Commissioning of an arc-melting / vacuum quench furnace facility for fabrication of Ni-Ti-Fe shape memory alloys, and their characterization, Thesis, University of Central Florida, USA, (2004).

Google Scholar

[6] ASM Handbook, Vol. 4 Heat treating, ASM international, (2002).

Google Scholar

[7] Atlas of Isothermal Transformation and Cooling Transformation Diagrams, American Society for Metals, p.181, (1977).

Google Scholar

[8] H. K. D. H. Bhadeshia, The lower bainite transformation and the significance of carbide precipitation, Acta Metallurgica, 28, 1103, (1980).

DOI: 10.1016/0001-6160(80)90093-0

Google Scholar

[9] F. G. Caballero, M. J. Santofimia, C. Garcı´a-Mateo and C. Garcı´a de Andre´s, Time-Temperature-Transformation Diagram within the Bainitic Temperature Range in a Medium Carbon Steel, Mater. Transactions, 45, 3272, (2004).

DOI: 10.2320/matertrans.45.3272

Google Scholar

[10] H. Bohlooli, M. Nakhaei, Comparasion of mechanical properties of bainite/ferrite dual phase 4340 steels with different percents of ferrite, World of Sciences Journal, 03, 161, (2013).

Google Scholar

[11] Atlas of Isothermal Transformation and Cooling Transformation Diagrams, American Society for Metals, p.369, (1977).

Google Scholar

[12] J. Xu, Y. Liu, S. Zhou, Calculation models of interlamellar spacing of Pearlite in high speed 82B rod, Journal of Iron and Steel Research International, 15, 57, (2008).

DOI: 10.1016/s1006-706x(08)60144-2

Google Scholar

[13] A. Kamyabi-Gol, M. Sheikh-Amiri, Spheroidizing Kinetics and Optimization of Heat Treatment Parameters in CK60 Steel Using Taguchi Robust Design, Journal of Iron and Steel Research International, 17, 45, (2010).

DOI: 10.1016/s1006-706x(10)60085-4

Google Scholar

[14] Practical Heat Treating, Second Edition, ASM International, (2006).

Google Scholar

[15] R.A. Grange, C.R. Hribal, and L.F. Porter, Hardness of Tempered Martensite in Carbon and Low-Alloy Steels, Μetallurgical Τransactions A, 8A, 1775, (1977).

DOI: 10.1007/bf02646882

Google Scholar

[16] Atlas of Isothermal Transformation and Cooling Transformation Diagrams, American Society for Metals, (1977).

Google Scholar

[17] K. Han, D.V. Edmonds, and G.D.W. Smith, Optimization of Mechanical Properties of High-Carbon Pearlitic Steels with Si and V Additions, Metallurgical and Materials Transactions A, 32, 1313, (2001).

DOI: 10.1007/s11661-001-0222-7

Google Scholar