Microwave Dielectric Properties of Ca[(Li1/3Nb2/3)0.95Zr0.15]O3+δ Ceramics with Ba2+ Substitution at A-Site
The microwave properties of (Ca1-xBax)[(Li1/3Nb2/3)0.95Zr0.15]O3+δ(0.0≤x≤0.2, CBLNZ) ceramics were investigated. A single phase with orthorhombic perovskite structure was obtained at x = 0.0 − 0.025. Both the εr and Qf value firstly increased with increasing Ba2+ content, and then began to decrease at x = 0.025. The τf value increased from −9.4 ppm/°C at x=0.0 to 18ppm/°C at x=0.2, which could be explained by the decrease of B-site bond valence in perovskite structure.
Wei Pan and Jianghong Gong
D. X. Zhou et al., "Microwave Dielectric Properties of Ca[(Li1/3Nb2/3)0.95Zr0.15]O3+δ Ceramics with Ba2+ Substitution at A-Site", Key Engineering Materials, Vols. 336-338, pp. 196-198, 2007