Textured PbTiO3 Based Ceramics Fabricated by Slip Casting in a High Magnetic Field
Textured PbTiO3 (PT) ceramics were fabricated by slip casting in a high magnetic field of 12 T. The sample obtained from the powder calcined at 1100 °C was (100), (010), and (001)-oriented, and the orientation factor was 90 %. On the other hand, the sample obtained from the powder calcined at 900 °C was not oriented. Aggregability and crystallinity of powder are an important factor when textured ceramics are fabricated by slip casting in a high magnetic field.