The Effect of TiC on the Liquid Phase Sintering of SiC Ceramics with Al₂O₃ and Y₂O₃ Additives

Abstract:

Low fracture toughness of SiC ceramics limits their applications for the low reliability. Inclusion of second ceramic phase improves the toughness of SiC ceramics. In this presentation, SiC ceramics with 5wt% TiC was pressureless liquid phase sintered (LPS) with the additives of Al₂O₃ and Y₂O₃ to ~98% theoretical density at the temperature of 1920 °C for 1 hour. The TiC grains were well distributed and good for the uniform distribution of the liquid phase YAG in the SiC matrix, which resulted in the homogeneous microstructure with fine SiC grains. The existence of TiC benefited the formation of elongated α-SiC, which favored the bridging and deflection of cracks so that the fracture toughness was improved to some extent. Because the amount of TiC was so small that the inherent properties of SiC was not degraded. The flexural strength and Vickers hardness maintained similar with the LPS SiC without TiC. The phase compositions detected in the sample were SiC, YAG and TiC. And no solid-solution of SiC and TiC was revealed by the mapping of EDS.

• Periodical: Key Engineering Materials (Volumes 602-603)
• Pages: 197-201
• DOI: https://doi.org/10.4028/www.scientific.net/KEM.602-603.197
• Online since: March 2014
• Authors: Han Qin Liang*, Xiu Min Yao, Hui Zhang, Xue Jian Liu, Zheng Ren Huang
• Keywords: Liquid Phase Sintering (LPS), Silicon Carbide (SiC), TiC, Toughening

References

[1] J Chen, W Li, W Jiang. Characterization of sintered TiC–SiC composites. Ceram Int. 2009; 35: 3125-9.

[2] O Borrero-Lopez, AL Ortiz, et al. Microstructural evolution and contact-mechanical properties of SiC ceramics prepared colloidally with low additive content. Ceram Int. 2012; 38: 5979-86.

DOI: 10.1016/j.ceramint.2012.04.051

[3] R Huang, H Gu, JX Zhang, DL Jiang. Effect Of Y2O3-Al2O3 ratio on inter-granular phases and films in tape-casting alpha-SiC with high toughness. Acta Mater. 2005; 53: 2521-9.

DOI: 10.1016/j.actamat.2004.10.055

[4] D Sciti, S Guicciardi, A Bellosi. Effect of annealing treatments on microstructure and mechanical properties of liquid-phase-sintered silicon carbide. J Eur Ceram Soc. 2001; 21: 621-32.

DOI: 10.1016/s0955-2219(00)00254-5

[5] D Bucevac, V Krstic. Microstructure–mechanical properties relations in SiC–TiB2 composite. Mater Chem Phys. 2012; 133: 197-204.

DOI: 10.1016/j.matchemphys.2012.01.007

[6] AL Ortiz, O Borrero-Lopez, et al. A route for the pressureless liquid-phase sintering of SiC with low additive content for improved sliding-wear resistance. J Eur Ceram Soc. 2012; 32: 965-73.

DOI: 10.1016/j.jeurceramsoc.2011.10.052

[7] A Can, M Herrmann, D McLachlan, I Sigalas, J Adler. Densification of liquid phase sintered silicon carbide. J Eur Ceram Soc. 2006; 26: 1707-13.

DOI: 10.1016/j.jeurceramsoc.2005.03.253

[8] F Rodriguez-Rojas, AL Ortiz, et al. Effect of Ar or N2 sintering atmosphere on the high-temperature oxidation behaviour of pressureless liquid-phase-sintered alpha-SiC in air. J Eur Ceram Soc. 2010; 30: 119-28.

DOI: 10.1016/j.jeurceramsoc.2009.08.004

[9] Y Luo, S Li, W Pan, L Li. Fabrication and mechanical evaluation of SiC–TiC nanocomposites by SPS. Mater Lett. 2004; 58: 150-3.

DOI: 10.1016/s0167-577x(03)00434-8

[10] R German, P Suri, S Park. Review: liquid phase sintering. J Mater Sci. 2009; 44: 1-39.

[11] D Bucevac, S Boskovic, B Matovic, V Krstic. Toughening of SiC matrix with in-situ created TiB2 particles. Ceram Int. 2010; 36: 2181-8.

DOI: 10.1016/j.ceramint.2010.06.001

[12] K Faber, A Evans. Crack deflection processes—I. Theory. Acta Metall Mater. 1983; 31: 565-76.

DOI: 10.1016/0001-6160(83)90046-9