The Characterization of Flame Cut Heavy Steel – The Residual Stress Profiling of Heat Affected Surface Layer

Abstract:

Flame cutting is commonly used thermal cutting method in metal industry when processing thick steel plates. Cutting is performed with controlled flame and oxygen jet, which burns steel and forms cutting edge. Flame cutting process is based on controlled chemical reaction between steel and oxygen at elevated temperature. Flame cutting of thick wear-resistant steels is challenging while it can result in cracks on and under the cut edge. Flame cutting causes uneven temperature distribution in the plate, which can introduce residual stresses. In addition, heat affected zone (HAZ) is formed and there both volume and microstructural changes as well as hardness variations are taking place. Therefore flame cutting always causes thermal stress, shape changes and consequently residual stresses to the material. Material behaviour under thermal and mechanical loading depends on the residual stress state of the material. Due to this, it is important to be able to measure the residual stresses. The aim of this study was to examine residual stresses on the cutting edge as a function of different flame cutting parameters. Also resulting microstructures and hardness values were verified. Varying parameters were the cutting speed, preheating and post heating procedures. Flame cut samples were investigated with X-ray diffraction method to produce residual stress profiles of the heat affected surface layer. Results indicated that different cutting parameters provide different residual stress profiles and that these profiles can be modified by changing the cutting speed and pre-or post-treatment procedures. Cutting parameters also affect the depth of the reaustenized region in the surface. The results correlate well with the actual industrial flame cutting and thus they provide an effective tool for optimizing the flame cutting process parameters.

• Periodical: Key Engineering Materials (Volume 674)
• Pages: 103-108
• DOI: https://doi.org/10.4028/www.scientific.net/KEM.674.103
• Online since: January 2016
• Authors: Tuomas Jokiaho*, Tuomo Saarinen, Suvi Santa-Aho, Pasi Peura, Minnamari Vippola
• Keywords: Flame Cutting, Heat Affected Zone, Heavy Steel Plate, Residual Stress, X-Ray Diffractometer

References

[1] R. Thiébaud, J. Drezet, J. Lebet, Experimental and numerical characterisation of heat flow during flame cutting of thick steel plates, J. Mater. Process. Tech. 214 (2014) 304-310.

DOI: 10.1016/j.jmatprotec.2013.09.016

[2] L.R. Soisson, Oxyfuel Gas cutting, Welding, Brazing, and soldering, Vol 6, ASM Handbook ASM International, (1993).

DOI: 10.31399/asm.hb.v06.a0001483

[3] HARDOX TechSupport, SSAB Oxelösund, (2007).

[4] L.E. Lindgren, A. Carlestam, M. Jonsson, Computational model of flame-cutting, J. Eng. Mater. Tech. 115 (1993) 440-445.

DOI: 10.1115/1.2904243

[5] A. Martín-Meizoso, J. Aldazabal, J.L. Pedrejón, S. Moreno, Resilience and ductility of Oxy-fuel HAZ cut, Frattura ed Integrita Strutturale 30 (2014) 14-22.

DOI: 10.3221/igf-esis.30.03

[6] W.E. Wood, Heat-affected zone studies of thermally cut structural steels. Publication No. FHWA-RD-93-015, U.S. Department of Transportation, Federal Highway Administration, (1994).

[7] H. Thomas, J. De Back, T.J. Bos, T. Muller, J.J.W. Nibbering, C.J.J.M. Verwey, R. Vonk, The Properties of flame-cut edges, Final report of Working Group 1913 of the Netherlands Institute of Welding, Technical steel research, Commission of the european communities, (1980).

[8] R. Thiébaud, J. Lebet, Experimental study of residual stresses in thick steel plates, Structural Stability Research Council, (2012).

[9] G.S. Schajer, (ed. ); Practical residual stress measurement methods, Wiley, (2013).

[10] J. Lu, (ed. ); Handbook of Measurement of Residual Stresses, Society for Experimental Mechanics Inc., The Farmont Press Inc., (1996).

[11] A.J. Perry, J.A. Sue, P.J. Martin, Practical measurement of the residual stress in coatings, Surf. Coat. Tech. 81 (1996) 17-28.

[12] D. Radaj, Heat effects of welding: temperature field, residual stresses, distortion; Berlin: Springer-Verlag, (1992).

[13] L.E. Lindgren, A. Carlestam, COMMP'93: International Conference on Computer-Assisted Materials design and Process Simulation, Nippon, Toshi Center, Tokyo, Japan, 1993, pp.141-146.

[14] Z.Y. Wei, Y.J. Liu, B. Zhou, Distributions and Influence Factors of Residual Stresses Induced by Oxygen Cutting Opening in Steel Structure, Adv. Mat. Res. 314-316 (2011) 437-447.

DOI: 10.4028/www.scientific.net/amr.314-316.437

[15] Non-destructive Testing. Test Method for Residual Stress analysis by X-ray Diffraction, SFS-EN 15305, Suomen Strandardisoimisliitto, SFS, Helsinki, (2008).