Investigation of Three-Dimensional Geometry of Butterfly Martensite and Analysis of Relationship between Hardness of Lath/Butterfly Two-Phase Martensite and its Grain Thickness in Medium-Carbon Steel

Abstract:

Medium-carbon steel with approximately 0.6 wt% carbon is widely used for mechanical applications, because the martensite contained in it is harder than that of low-carbon and high-carbon steel. The microstructure of steel martensite varies depending on the carbon content, and the microstructure of medium-carbon steel martensite are a mixture of lath martensite (LM) and butterfly martensite (BM). The geometry of LM grains are thin plates having thicknesses of 0.2–0.5 μm. As for BM, some researches demonstrated that the region of martensite spreads in the depth direction of the observation surface. However, the three-dimensional geometry of BM grains remains unclear. Through cross-sectional observation using focused ion beam (FIB), the present study demonstrates that one BM grain is formed via collision of two plates. Previous research shows that the hardness of LM is inversely correlated with the thickness of the grains. The FIB observation result indicates that geometry of LM and BM grains are both plate-like. In the present study, whether the same relationship is valid for the mixture of LM and BM grains is investigated. The results show that the hardness of medium-carbon steel martensite increases according to the decrease in thickness of constituent grains of the two-phase structure of LM and BM.

• Periodical: Materials Science Forum (Volume 1016)
• Pages: 1039-1044
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.1016.1039
• Online since: January 2021
• Authors: Takayoshi Niho*, Keisuke Nagato, Masayuki Nakao
• Keywords: Ausforming, Butterfly Martensite, Hardness, Microstructure, Three-Dimensional Geometry

References

[1] T. Maki, Morphology and substructure of martensite in steels, in Phase Transformations in Steels, 2 (2012) 34–58.

DOI: 10.1533/9780857096111.1.34

[2] D. J. Schmatz and V. F. Zackay, Mechanical properties of deformed metastable austenitic ultra high strength steel, Trans. ASM, 51 (1959) 476-494.

[3] P. H. Shipway and H. K. D. H. Bhadeshia, The effect of small stresses on the kinetics of the bainite transformation, Mater. Sci. Eng. A, 201(1995), 143-149.

DOI: 10.1016/0921-5093(95)09769-4

[4] M. Omori, On the Mechanical Properties and fatigue strength of mn-cr-b spring steel in consequence of its thermomechanical treatment by gradually cooling it, J. Soc. Mater. Sci. Japan, 20 (1971) 1024-1030, (in Japanese).

DOI: 10.2472/jsms.20.1024

[5] J. P. Naylor, The influence of the lath morphology on the yield stress and transition temperature of martensitic- bainitic steels, Metall. Trans. A, 10 (1979), 861-873.

DOI: 10.1007/bf02658305

[6] S. Morito, H. Yoshida, T. Maki, and X. Huang, Effect of block size on the strength of lath martensite in low carbon steels, Mater. Sci. Eng. A, 438 (2006) 237-240.

DOI: 10.1016/j.msea.2005.12.048

[7] H. Sato, T. Sonoda, T. Moritani, S. Zaefferer, and Y. Watanabe, Microstructural analysis of butterfly-type martensite by using EBSD, Hyomen Kagaku, 36 (2015) 172-177, (in Japanese).

DOI: 10.1380/jsssj.36.172

[8] E. O. Hall, The deformation and ageing of mild steel: II Characteristics of the Lüders deformation, Proc. Phys. Soc. Sect. B, 64 (1951) 742-747.

DOI: 10.1088/0370-1301/64/9/302

[9] N. J. Petch, The cleavage strength of polycrystals, J. Iron Steel Inst., 174 (1953), 25-28.

[10] https://www.3ds.com/products-services/simulia/products/abaqus/.

[11] F. Furumura, T. Ave, W. J. Kim, and T. Okabe, Nonlinear Elasto-plastic creep behavior of structural steel under continuously varying stress and temperature, J. Struct. Constr. Eng., 353 (1985), 92-102.

DOI: 10.3130/aijsx.353.0_92

[12] A. Shibata, T. Nagoshi, M. Sone, S. Morito, and Y. Higo, Evaluation of the block boundary and sub-block boundary strengths of ferrous lath martensite using a micro-bending test, Mater. Sci. Eng. A, vol. 527 (2010) 7538-7544.

DOI: 10.1016/j.msea.2010.08.026