Giant Magnetoimpedance in Fe89B4Hf7 Nanocrystalline Ribbons

Xiaojun Yu; Ji Fan Hu; Dongling Wang; Hong Wei Qin; Bo Li

doi:10.4028/www.scientific.net/MSF.475-479.2203

Paper Titles

Nd₂Fe₁₄B/α-Fe Nanocomposites Prepared by Mechanically Activated Disproportionation and Subsequent Desorption-Recombination
p.2185

Magneto-Transport Study on Ni_1-xMn_x(0.23<x<0.3) in High Fields up to 30T
p.2189

Magnetic Properties of Ni-Zn Ferrite Ceramics Prepared from the Blend of Powders
p.2193

Growth and Properties of Half-Metallic Double Perovskite Thin Films
p.2197

Giant Magnetoimpedance in Fe₈₉B₄Hf₇ Nanocrystalline Ribbons
p.2203

Magnetoresistance and Current-Controlled Electric Transport Properties of Fe-C Film on Si Substrate
p.2207

Magnetoresistance in the Hard/Cu/Soft Sandwiches: Dependence on Layer Thickness and Field Annealing
p.2211

Synthesis and Magnetic Properties of FeCo Alloy Nanoparticles by Hydrogen Plasma Metal Reaction
p.2215

Giant Magnetoimpedance in as Quenched Fe Based Nanocrystalline Ribbons
p.2219

HomeMaterials Science ForumMaterials Science Forum Vols. 475-479Giant Magnetoimpedance in Fe89B4Hf7...

Giant Magnetoimpedance in Fe₈₉B₄Hf₇ Nanocrystalline Ribbons

Abstract:

In this work the giant magnetoimpedance effect has been found in Fe89B4Hf7 nanocrystalline ribbons. There is an optimal annealing temperature about 650°C for obtaining a large magnetoimpedance. The magnetoimpedance can reach 208% for Fe89B4Hf7 annealed at 650°C for 20min. meanwhile, it has been found that the magnetoimpedance in FeHfB shows a good thermal- heating stability, which is useful for application.

You might also be interested in these eBooks

View Preview

Info:

Periodical:

Materials Science Forum (Volumes 475-479)

Pages:

2203-2206

DOI:

https://doi.org/10.4028/www.scientific.net/MSF.475-479.2203

Citation:

Cite this paper

Online since:

January 2005

Authors:

Xiaojun Yu, Ji Fan Hu, Dongling Wang, Hong Wei Qin, Bo Li

Keywords:

Magnetoimpedance, Nanocrystalline Ribbons, Permeability

Export:

RIS, BibTeX

Price:

Permissions CCC:

Request Permissions

Permissions PLS:

Request Permissions

Сopyright:

Citation:

References

[1] K. Mohri, K. Kawashima, Y. Yoshida, L.V. Panina, IEEE Trans. Magn., 1992, 28(5): 3150-3152.

DOI: 10.1109/20.179741

Google Scholar

[2] L.V. Panina, K. Mohri, K. Bushida, M. Noda, J. Appl. Phys., 1994, 76(10): 6198-6203.

Google Scholar

[3] R.S. Beach, A.E. Berkowitz, Appl. Phys. Lett., 1994, 64 (26): 3652-3654.

Google Scholar

[4] J. Hu, L. Zhang, H. Qin, Y. Wang, Z. Wang, S. Zhou, J. Phys. D: Appl. Phys., 2000, 33 (5) : L45-L47.

Google Scholar

[5] M. Knobel, J. Schoenmaker, J.P. Sinnecker, R. Sato Turtelli, R. Grössinger, W. Hofsteter, H. Sassik, Mater. Sci. Eng., 1997, A226-228: 546-549.

DOI: 10.1016/s0921-5093(96)10682-1

Google Scholar

[6] J. Hu, S. Zhou, W. Chen, Y. Wang, Solid State Communi., 1999, 109(10): 661-664.

Google Scholar

[7] K. S. Byon, S.C. Yu, J.S. Kim, IEEE Trans. Magn. 36(2000)3439.

Google Scholar

[8] P. Aragoneses, D. Holzer, H. Sassik, A. Zhukov, R. Frossinger, J. Gonzalez, J. Magn. Magn. Mater, 203(1999)292.

Google Scholar

[9] B. Li, J. Hu, H. Qin, N. Ma, K. An, X. Wang, J. Iron & Steel Res. Int., 10(2003)55.

Google Scholar

[10] A. Makino, T. Hatanai, A. Inoue, T. Masumoto, Mater. Sci. Eng., A226-228(1997)594.

Google Scholar

[11] M. Vázquez, J.M. Garcia-Beneytez, J. P. Sinnecker, L. Li, J. Appl. Phys., 83(1998)6578.

Google Scholar

[12] J. Hu, H. Qin, F. Zhang, R. Zheng, J. Appl. Phys., 91(2002)7418.

Google Scholar

[13] J. Hu, H. Qin, L. Zhang, J. Chen, Mater. Sci. Eng. B, 106(2004)202.

Google Scholar