Influence of Oxide Additions in Cu-Co-Fe Composite Powders Obtained by Mechanical Alloying

Abstract:

Nanocrystalline composite powders were prepared by mechanical alloying of pure Cu, Fe and Co as metallic major part and Al₂O₃ or Fe₂O₃ or SiO₂ as ceramic reinforcement in a high-energy ball mill. Alloys of the copper-iron-cobalt system are promising for the development of new materials and applications. Cu-Fe-Co is used in different applications depending on the properties required. These can be related for example to toughness when used as rock cutting tool, to magnetic and electric properties for microelectronics or to chemical behaviour when used as catalysts in bioalcohol production industry. The objective of the present study is to contribute to understanding how and to which amount the ceramic reinforcement affects the properties for which this Cu-Fe-Co system is used as well as to envisage other less frequently uses for the composite powders. Structural and magnetic transformations occurring in the material during milling were studied with the use of X-ray diffraction, scanning quantum induction device (SQUID) and magnetic force microscopy (MFM). In mechanical alloying the transformations depend upon milling time. The results showed that milling the elemental powders of Cu-Fe-Co in the mass proportion of 50:25:25 respectively for times up to 10h leads to the progressive dissolution of Fe and Co atoms into FCC Cu and the final product of the MA process was the nanocrystalline Cu containing Fe and Co with a mean crystallite size (from coherent crystal size determination by diffraction) of 20 nm aprox. When ceramic particles are milled together with the metals (at proportions of the oxides between 1-10%) this mechanism is retarded. On the other hand, the lowest mean crystallite size is reached without ceramic particles in the milling process. However the composite powder produced in all the cases stabilized similar lowest crystallite size between 45-50 nm. Mechanically alloyed metallic-ceramic composite powder showed lower saturation magnetization than the metallic system but enhanced coercive field (significantly for hematite reinforcement). All the studied systems are intermediate ferromagnetics (H_c≈104 A/m). Milling time significantly affects the structure, composition and properties for both metallic and composite systems.

• Periodical: Materials Science Forum (Volumes 783-786)
• Pages: 1548-1553
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.783-786.1548
• Online since: May 2014
• Authors: Nuria Llorca-Isern*, Cristina Artieda-Guzman, Jose Alberto Vique, Antoni Roca
• Keywords: Catalyst, Ceramic Reinforcement, Composite Powder, Cu-Fe-Co, Magnetic Property, Mechanical Milling, Microelectronics

References

[1] R. Koohkan, S. Sharafi, H. Shokrollahi, K. Janghorban, Preparation of nanocrystalline Fe-Ni powders by mechanical alloying used in soft magnetic composites, J. Magn. Magn. Mater. 320 (2008) 1089-1094.

DOI: 10.1016/j.jmmm.2007.10.033

[2] R. Hamzaoui, O. Elkedim, N. Fenineche, E. Gaffet, J. Craven, Structure and magnetic properties of nanocrystalline mechanically alloyed Fe-10% Ni and Fe-20%Ni, Mat. Sci. Eng. 360 (2003) 299-305.

DOI: 10.1016/s0921-5093(03)00460-x

[3] B. Bhoi, V. Srinivas, Vidyadhar Singh, Evolution of microestructure and magnetic properties of nanocrystalline Fe70-xCuxCo30 alloy prepared by mechanical alloying, J. Alloys Compd. 496 (2010) 423-428.

DOI: 10.1016/j.jallcom.2010.01.155

[4] R. Lardé, J.M. Le Breton, X. Sauvage, Investigation of the chemical homogeneity of Cu80(Fe, Co)20 powders produced by mechanical milling, J. Alloys Compd. 474 (2009) 52-56.

DOI: 10.1016/j.jallcom.2008.07.027

[5] M. Azabou, H. Ibn Gharsallah, L. Escoda, J.J. Suñol, A.W. Kolsi, M. Khitouni, Mechanochemical reactions in nanocrystalline Cu-Fe system induced by mechanical alloying in air atmosphere, Powder Metall. 224 (2012) 338-344.

DOI: 10.1016/j.powtec.2012.03.016

[6] C. Liu, T.R. Cundari, A.K. Wilson, CO2 Reduction on Transition Metal (Fe, Co, Ni, and Cu) Surfaces: In Comparison with Homogeneous Catalysis, The journal of Physical Chemistry C, 116 (2012) 5681-5688.

DOI: 10.1021/jp210480c

[7] B. Wang, Recent development of non-platinum catalysts for oxygen reduction reaction, J. Power Sources 152 (2005) 1.

DOI: 10.1016/j.jpowsour.2005.05.098

[8] H. Tributsch, U. I. Koslowski, I. Dorbandt, Experimental and theoretical modeling of Fe-, Co-, Cu-, Mn-based electrocatalysts for oxygen reduction, Electrochemica Acta, 53 (2008) 2198-2209.

DOI: 10.1016/j.electacta.2007.09.027

[9] C. Artieda-Guzman, N. Llorca-Isern, Magnetic behaviour of nanocrystalline Cu–Fe–Co/Al2O3 composite powders obtained by mechanical alloying, J. Alloys Compd. 580 (2013) 276-283.

DOI: 10.1016/j.jallcom.2013.05.069

[10] O. Öztürk, S. Okur, L. Pichon, M.O. Liedke, J.P. Riviere, Magnetic layer formation on plasma nitrided CoCrMo alloy, Surf. Coat. Tech. 205 (2011) 280–285.

DOI: 10.1016/j.surfcoat.2011.01.047

[11] G.F. Korznikova, Domain structures of ultrafine grained ferromagnets achieved by severe plastic deformation or melt quenching, J. Microsc. 239 (2010) 239-244.

DOI: 10.1111/j.1365-2818.2010.03372.x

[12] D. Płusa, M. Dospiał, D. Derewnicka-Krawczynska, P. Wieczorek, U. Kotlarczyk, The domain structure of die-upset anisotropic magnet based on Nd-(Fe, Co)-B alloy, Arch. Metall. Mater. 56 (2011) 159-161.

DOI: 10.2478/v10172-011-0018-8

[13] W. Laslouni, K. Taibi, D. Dahmoun, M. Azzaz, Structure and properties of nanocrystalline Cu70Fe18Co12 obtained by mechanical alloying, J. Non Cry. Sol. 353 (2007) 2090-(2093).

DOI: 10.1016/j.jnoncrysol.2007.01.072