Influence of Strain Path on Work Hardening and Texture in an Austenitic Stainless Steel

Article Preview

Abstract:

The effect of strain path on work hardening and texture for a super austenitic stainless steel was investigated using both experiments and modeling. Compression deformation tests by stepwise changing loading direction in two and three dimensions were performed on cubic specimens at room temperature. The results were compared to uniaxial compression with equal accumulative strain, up to 20%, and uniaxial tension with equal final strain, up to 10% elongation of the longest side. The textures in all samples were analyzed using pole figures from EBSD analysis. Because of the high stacking fault energy of this super austenitic stainless steel, the texture was dominated by <110>-fiber texture in the compressive direction for the uniaxial compression, <111>- and <100>-fiber texture in the tensile direction for the uniaxial tensile test, and a combination of all these for the cube deformation. The density of the texture was much weaker for samples where the loading direction altered, if samples with equal accumulated strain were compared. The cube deformation was also modeled using a crystal plasticity model. The crystal plasticity model consists of a representative volume element (RVE) containing crystal grains with random orientations. The Taylor assumption was used for homogenization between the macro-and subscale. The material parameters in the crystal plasticity model were determined by calibration of its macroscopic response to experimental data. The simulated textures correspond rather well to the experimental results, but the work hardening should be completed to take into account kinematic hardening.

You might also be interested in these eBooks

Info:

Periodical:

Materials Science Forum (Volumes 783-786)

Pages:

2567-2572

Citation:

Online since:

May 2014

Export:

Price:

Permissions CCC:

Permissions PLS:

Сopyright:

© 2014 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

* - Corresponding Author

[1] L.F. Coffin and J.F. Tavernelli: Trans. Met. Soc. AIME 215 (1959), pp.794-807.

Google Scholar

[2] P.E. Armstrong and J.E. Hockett: J. Mech. Phys. Solids Vol. 30 (1982), pp.37-58.

Google Scholar

[3] D. Gonzalez, J.F. Kelleher, J. Quinta da Fonseca and P.J. Withers: Mat. Sci. Eng. A Vol 546 (2012) 263-271.

Google Scholar

[4] G.I. Taylor: J. Inst. Met. 62 (1938), pp.307-324.

Google Scholar

[5] G. Sachs: Z. Ver. Deu. Ing. 72-22 (1928), p.734.

Google Scholar

[6] J.W. Hutchinson: Proc. Roy. Soc. Lond. A Vol. 319 (1970), p.247.

Google Scholar

[7] B. Clausen: Characterisation of Polycrystal Deformation by Numerical Modelling and Neutron Diffraction Measurements, Riso-R-985(EN), Riso National Laboratory, Roskilde, Denmark, (1997).

Google Scholar

[8] F. Roters, P. Eisenlohr, L. Hantcherli, D.D. Tjahjanto, T.R. Bieler and D. Raabe: Acta Materialia Vol. 58 (2010), pp.1152-1211.

DOI: 10.1016/j.actamat.2009.10.058

Google Scholar

[9] S.R. Kalidindi, C.A. Bronkhort and L. Anand: J. Mech. Phys Vol. 40. (1992), pp.537-569.

Google Scholar

[10] R.J. Asaro and A. Needleman: Acta metal. Vol. 33 (1985), p.923.

Google Scholar

[11] U.F. Kocks and H. Mecking: Prog. Mat. Sci. Vol. 48 (2003), pp.171-273.

Google Scholar

[12] R. Lillbacka, On the multiscale modeling of duplex stainless steels, PhD thesis, Chalmers, Gothenburg, Sweden, (2007).

Google Scholar

[13] M. Ekh, R. Lillbacka and K. Runesson: Int. J. Plast. Vol. 20 (2004), pp.2143-2159.

Google Scholar