Microstructural and Mechanical Properties of the Intercritically Reheated Coarse Grained Heat Affected Zone (ICCGHAZ) of an API 5L X80 Pipeline Steel

Abstract:

The weld thermal cycle, depending on the welding process and steel composition can reduce the toughness of the HAZ when compared with the base metal. In the intercritically reheated coarse grained HAZ (ICCGHAZ) region, microstructural transformations from coarse austenite to bainite or martensite are liable to occur. Reheating into the dual phase field temperature and subsequent cooling can lead to the formation of “microphases” commonly referred to Martensite-Austenite (MA) constituent. Due to the C enrichment of the austenite, this region is regarded as local brittle zones (LBZ) and degradation of HAZ toughness can be attributed to the formation of local brittle zones (LBZ) at the ICCGHAZ. This work will discuss the characteristics of the ICCGHAZ of two API5LX80 steels produced by thermomechanical controlled process (TMCP) without accelerated cooling using a finishing rolling temperature in the dual phase field, where the main hardening mechanisms are grain refining and precipitation. Weld thermal cycle simulation, using a Gleeble 3800®, characterised by the peak temperature (Tp) of 800oC and the cooling time from 800 to 500oC (∆t800–500) were applied in order to obtain an ICCGHAZ equivalent to a 2.5, 3 and 4kJ/mm heat input. Charpy-V tests and metallographic analysis using optical and electron microscopy were carried out to evaluate the simulated zone. The results have shown that the ICCGHAZ presented a necklace microstructure at the prior austenite grain boundaries associated with the low impact energy and the presence of the MA microconstituent.

• Periodical: Materials Science Forum (Volumes 783-786)
• Pages: 657-662
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.783-786.657
• Online since: May 2014
• Authors: J.L.M. Andia*, Luís Felipe Guimarães de Souza, Ivani de Souza Bott
• Keywords: API 5L X80, Girth Weld, ICCGHAZ, Physical Simulation, Weld Thermal Cycle

References

[1] S. Moeinifar, A.H. Kokabi, H.R. Madaah Hosseini, Influence of Peak Temperature During Simulation and Real Thermal Cycles on Microstructure and Fracture Properties of the Reheated Zones, Materials and Design 31 (2010) 2948–2955).

DOI: 10.1016/j.matdes.2009.12.023

[2] H L Li, X Li, L K Ji. Strain-based Design for Pipeline and Development of Pipe Steels with High Deformation Resistance [J]. Welded Pipe and Tube, 2007, 9(5): 5-11.

[3] N Shikanai, S Mitao, S Endo. Recent Development in Microstructural Control Technologies through the Thermomechanical Control Process (TMCP) with JFE Steel's High-Performance Plates[R]. JFE Technical Report, 2007, 18: 1-6.

[4] Jennifer M. Reichert, Thomas Garcin, Matthias Militzer, Warren J. Poole, Formation of Martensite/Austenite (M/A) in X80 Linepipe Steel, Proceedings of the 2012 9th International Pipeline Conference IPC2012 September 24-28, 2012, Calgary, Alberta, Canada , IPC2012-90465.

DOI: 10.1115/ipc2012-90465

[5] C.L. Davis and J.E. King, Effect of Cooling Rate on Intercritically Reheated, Materials Science and Technology, 9(1993), 8-15.

[6] Peyman Mohseni, Brittle and Ductile Fracture of X80 Arctic Steel, PhD Thesis, Norwegian University of Science and Technology, Faculty of Natural Sciences and Technology, Department of Materials Science and Engineering, Trondheim, October (2012).

[7] Y. Li, D. N. Crowther, M. J. W. Green, P. S. Mitchell and T. N. Baker, The Effect of Vanadium and Niobium on the Properties and Microstructure of the Intercritically Reheated Coarse Grained Heat Affected Zone in Low Carbon Microalloyed Steels, ISIJ International, Vol. 41 (2001).

DOI: 10.2355/isijinternational.41.46

[8] X. Zhang, H. Gao, A Study of Impact Toughness of Intercritically Reheated Coarse Grain Heat Affected Zone of Two Type X80 Grade Pipeline Steel, Transaction of JWRI, Special Issue WSE 2011, 2011, 101 -104.

[9] H. K. D. H. Bhadeshia, Very Short and Very Long Heat-Treatments in the Processing of Steel, Thermomechanical Simulation and Processing of Steels, Simpro 08, eds S. K. Chaudhuri, B. K. Jha, S. Srikant, P. K. Maini, A. Deva, R. Datta, Allied Publishers Pvt. Ltd., Kolkata, India, (2008).

[10] P. Harrison, P. Wall, Effect of alloying elements on HAZ microstructure and toughness, Report , EUR 15834 EN, Technical steel research : properties and service performance, ISBN 92-827-7203-9, (1996).

[11] N. Isasti, D. Jorge-Badiola, M.L. Taheri, B. Lopez, and P. Uranga, Effect of Composition and Deformation on Coarse-Grained Austenite Transformation in Nb-Mo Microalloyed Steels, Metallurgical and Materials Transactions A, Volume 42A, December 2011, 3729-3742.

DOI: 10.1007/s11661-011-0624-0

[12] J.Y. Koo, M.J. Luton , N.V. Bangaru, R. A. Petkovic, D.P. Fairchild, C.W. Petersen, H. Asahi, T. Hara, Y. Terada, M. Sugiyama, H. Tamehiro, Y. Komizo, S. Okaguchi, M. Hamada, A. Yamamoto, I. Takeuch, Metallurgical Design of Ultra-High Strength Steels for Gas Pipelines, Proceedings of The Thirteenth (2003).

[13] A. D. Batte, P. J. Boothby, and A. B. Rothwell, Understanding the Weldability of Niobium-Bearing HSLA Steels, in Niobium Science & Technology, edited by P. J. P. Bordignon, T. Carneiro, J. Duncombe, D. Howden, K. Hulka, A. Issa Filho, S.R. Keown, C. Klinkenberg, W. B. Morrison, J. Patel, A. T. Pereira, B. F. Riffel, F. Siciliano, and G. Tither (Niobium 2001Ltd., Bridgeville, PA, 2002), pp.931-958.

[14] K. Poorhaydari, B. M. Patchett, and D. G. Ivey, Estimation of Cooling Rate in the Welding of Plates with Intermediate Thickness, Welding Journal, Supplement to the Welding Journal, October 2005, 149 –s - 155 –s.