The Study of Carbon Materials Prepared by Zhaotong Anthracite under Ultra-High Temperature

Abstract:

In this paper, reporting a new way to directly prepare quality of carbon materials such as artificial graphite, like-graphitization carburant and senior carbonaceous reductant et al ,which is prepared from anthracite under ultra-high temperature without any other additional process and catalyst. The chemical composition of carbon materials was analysed ; the electrical resistivity was tested; the composition of phase and the graphitization degree was tested by XRD; the microstructure was characterized by SEM and the degree of crystallization and crystal defect was characterized by the Raman diffraction spectrum. At the same time, the graphitization method was discussed during ultra-high temperature. The results show that good carburant and carbonaceous reductant can be prepared by anthracite which was graphitization under ultra-high temperature ;The microstructure of carbon materials which was prepared by anthracite that was graphitization during ultra-high temperature is more ordered than that of raw anthracite, its graphitization degree also increase significantly; When the ultra-high graphitization temperature is above 2600 °C, carbon materials which is like to pure graphite have a small amount of structural defects and distortion; the high quality carbon materials prepared by graphitization method under ultra-high temperature ,it is a simple process with low cost and high added value, and its prospects of application is broad.

• Periodical: Materials Science Forum (Volumes 809-810)
• Pages: 807-814
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.809-810.807
• Online since: December 2014
• Authors: Jia Qing Yang, Shu He Lu*, Xiao Hu Hua, Xiao Gang Wang, Li Bin Niu, Zi Min Fan, Jia Bo Wang
• Keywords: Carbon Materials, Graphitization, Ultra-High Temperature, Zhaotong Anthracite

References

[1] X.Z. Wang,N. Liu, and H. Hu, etc: Journal of new carbon materials. Vol. 29(2014)No. 2, pp.81-85(In Chinese).

[2] L.L. Zhou, C. Liu: Proceedings of the CSEE. Vol. 31(2014)No. 2, pp.7-16(In Chinese).

[3] T.Q. Li,J.S. Wang andZ.J. Hu, etc: Aerospace material craft. Vol. 73(2006)No. 2, pp.1-8(In Chinese).

[4] Y. Xu, Y. Wang, W. guo, etc: Journal of research and prospect of coal in yunnan province. Vol. 53(2006)No. 1, pp.28-32(In Chinese).

[5] L.Q. Ma, Y.K. He, S.X. Huang, etc: Carbon techniques. Vol. 23(2004)No. 2, pp.40-45(In Chinese).

[6] Q.L. Li , W . Guo: Journal of coal processing and comprehensive utilization. Vol. 140(2012)No. 2, pp.28-32(In Chinese).

[7] Ferrous metallurgy industry standard of China. The steelmaking carburant. YB/T192-(2001).

[8] Y.J. Xu: Journal of coal processing and comprehensive utilization. Vol. 147(2013)No. 3, pp.60-65 (In Chinese).

[9] B.L. Zhang: Journal of nonferrous mining and metallurgy. Vol. 17(2001)No. 5, pp.33-36 (In Chinese).

[10] G.J. Ma, Z.J. Yang, N. Zhao, etc: Journal of coal processing and comprehensive utilization. Vol. 29 (1993)No. 5, pp.29-34(In Chinese).

[11] Z. Ning: Ferro-Alloys 2009. Vol. 201(2008)No. 4, pp.14-20(In Chinese).

[12] J.C. Duan ,X.G. Zhuang, M.C. He: Journal of geological science and technology intelligence. Vol. 21(2002)No. 2, pp.65-70(In Chinese).

[13] Martinez M T, Callejas M A, Benito A M, et. al: Carbon. Vol. 39(2001)No. 8, pp.1251-1255.

[14] D.F. Li,H.J. Wang X.K. Wang. Spectroscopy and spectral analysis. Vol. 17(2001) No. 11, pp.2249-2254.