Effect of Aging Treatment Technology on Properties of Al-Mg-Si-Cu-Zr-Er Alloy for Auto Sheets

Abstract:

The effect of natural aging, pre-aging and paint-bake aging technology on properties of Al-Mg-Si-Cu-Zr-Er alloy for auto sheets was investigated by performance testing, microstructure observation, and differential thermal analysis. The results showed that the natural aging alloy before and after paint-bake aging presented the double peaks feature of both the mechanical properties and hardness, the maximum value of strength and hardness appeared on the second aging peak, and the paint-bake aging softening occurred. The result of differential thermal analysis showed that, compared with the artificial aging, the precipitation of β′′ phase was delayed after the natural aging; the precipitates were mainly β′′ nuclei at the paint-bake aging, and it is difficult to achieve paint-bake aging hardening. After pre-aging and nature aging treatment, the precipitates were mainly composed of β′′ phase at the paint-bake aging, and the paint-bake aging hardening was realized. The addition of Er and Zr elements accelerated the precipitation of β′′ phase, the precipitation temperature of β′′ phase reduced and the time of the first natural aging peak and pre-aging was shortened. The parameters of pre-aging treatment of alloy sheets was solution and water quenching, and then age at 170 °C for 5 min.

• Periodical: Materials Science Forum (Volume 850)
• Pages: 815-822
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.850.815
• Online since: March 2016
• Authors: Qian Zhao, Xiao Guang Yuan, Hong Jun Huang, Peng Zhao
• Keywords: Al-Mg-Si Alloy, Natural Aging, Pre-Aging, Properties

References

[1] C. Booth-Morrison, D. N Seidman, D.C. Dunand, Effect of Er additions on ambient and high-temperature strength of precipitation-strengthened Al-Zr-Sc-Si alloys, Acta. Mater. 60 (2012) 3643-3654.

DOI: 10.1016/j.actamat.2012.02.030

[2] N.Q. Vo, D.C. Dunand, D.N. Seidman, Improving aging and creep resistance in a dilute Al-Sc alloy by microalloying with Si, Zr and Er, Acta. Mater. 63 (2014) 73-85.

DOI: 10.1016/j.actamat.2013.10.008

[3] D.X. Yang, X.Y. Li, D.Y. He, H. Huang, Effect of minor Er and Zr on microstructure and mechanical properties of Al-Mg-Mn alloy (5083) welded joints, Mater. Sci. Eng. A. 561(2013) 226-231.

DOI: 10.1016/j.msea.2012.11.002

[4] S.P. Wen, K.Y. Gao, Y. Li, H. Huang, Z.R. Nie, Synergetic effect of Er and Zr on the precipitation hardening of Al-Er-Zr alloy, Scr. Mater. 65(2011) 592-595.

DOI: 10.1016/j.scriptamat.2011.06.033

[5] X.F. Huang, Y. Gao, P. Wu, X.N. Chen, B. Li, G.Z. Li, J.Y. Xu, Microstructures and properties of 6063 aluminium alloy as-cast modified by rare earth element Er, Heat. Treat. Met. 36(2011) 21-24.

[6] X.G. Yuan, Q. Zhao, W. Zheng, Y.Y. Qin, H.L. Li, H.J. Huang, The new AlMgSi alloy sheets and preparation method, China. Patent 201110025847. 1. (2011).

[7] M. Jin, G.J. Shao, Effect of Cu on precipitation phases at early stage in 6082 Al-Mg-Si ally aged, Chin. J. Nonferrous. Met. 19(2009) 1-7.

[8] Y.N. Liu, J.H. Chen, M.J. Yin, C.H. Li, C.L. Wu, X.Q. Zhao, The influences of natural ageing and Cu addition on the age hardening behavior of AlMgSi(Cu) alloys, J. Chin. Electr. Microse. Soc. 29(2010) 280-286.

[9] Y.A. Pan, Z.Y. Chen, H. Huang, S.P. Lin, Z.R. Nie, Age behavior of Al-4. 9Zn-1. 6Mg-0. 4Mn-0. 1 Zr-xEr alloy, Chin. J. Rare. Met. 35(2011) 6-11.

[10] B.Z. Xing, S.P. Lin, S.P. Wen and Z.R. Nie, Existing forms and affection of trace amount element erbium and zirconium on AA5083 alloy, J. Chin. Rare. Earth. Soc. 29(2011) 158-162.

[11] M. Murayama, K. Hono, Pre-precipitate clusters and precipitation processes in Al-Mg-Si alloys, Acta Mater. 47(1999) 1537-1548.

DOI: 10.1016/s1359-6454(99)00033-6

[12] Y. Birol. Pre-aging to improve bake hardening in a twin-roll cast Al-Mg-Si alloy, Mater. Sci. Eng. A. 391(2005) 175-180.

DOI: 10.1016/j.msea.2004.08.069

[13] H. Liu, W.J. Song, G. Zhao, C.M. Li, L. Zuo, Pre-aging and microstructures properties on 6000 series aluminium alloys for automotive body sheets, Chin. J. Nonferrous. Met. 15(2005) 270-276.

[14] J.N. Feng, J.H. Chen, C.H. Liu, Y.F. Liao, X.L. Li, Effects of pre-aging treatments on the microstructures and properties before and after paint bake cycle for a 6016 aluminum alloy, J. Chin. Electr. Microse. Soc. 31(2012) 461-468.

[15] L. Ying, G.Z. Shen, P. Hu, A.D. Wang, N. Ma, Y. Chang, Research on bake hardening behavior of AA6016 aluminum alloy sheets, J. Mech. Eng. 47(2011) 19-24.

DOI: 10.3901/jme.2011.10.019

[16] W.F. Miao, D.E. Laughlin. A differential scanning calorimetry study of aluminum alloy 6111 with different pre-aging treatments, J. Mater. Sci. Lett. 19(2000) 201-203.

[17] D.J. Bryant. The effects of preaging treatments on aging kinetics and mechanical properties in AA6111 aluminum autobody sheet, Metall. Mater. Trans. A. 30(1999) 1999-(2006).

DOI: 10.1007/s11661-999-0010-3

[18] Y.G. An, H. Vegter, L. Zhuang, A. Hurkmans, Fast aging kinetics of the AA6016 Al-Mg-Si alloy and the application in forming process, Metall. Mater. Trans. A. 33(2002) 3121-3126.

DOI: 10.1007/s11661-002-0297-9

[19] J.B. Zhang, Y.A. Zhang, Z.B. He, L.B. Jin, B.H. Zhu, Z.H. Li, Effect of natural ageing on properties and microstructure of 7N01 aluminum alloys, Chin. J. Rare Met. 36(2012) 191-195.

[20] L.L. Ge, Y.B. Li, X. Lu, Y.S. Zhou, Y.W. Guo, Research on pre-aging treatment of 6016 automotive aluminum sheet, Forg. Stamp. Technol. 39(2014) 113-117.

[21] P.C. Li, M.P. Wang, X.H. Sun, G.F. Xu, Study of ageing of Al-Mg-Si alloys, J. Cent. South. Univ. Technol. 29(1998) 262-265.

[22] H. Liu, G. Zhao, C.M. Liu, L. Zuo, Artificial aging precipitation behavior of 6000 series alloys naturally aged and pre-aged, Trans. Mater. Heat. Treat. 29(2008) 74-78.

[23] Q.M. Gao, S.F. Yan, X.H. Xiong, Aging-harding of 6111 aluminum alloy, Heat. Treat. Met. 34(2009) 86-88.

[24] X.N. Wang, S.C. Li, Z.Q. Zheng, B. Cai, Z.Q. Liao, Effect of pre-aging on formative and mechanical properties of 6022 aluminum alloy, Mater. Sci. Eng. Pow. Metall. 16(2011) 20-25.

[25] N. Tian, G. Zhao, J.J. Wang, T. Huang, B. Nie, L. Zuo, C.M. Liu, Pre-aging treatment of Al-Mg-Si aluminum alloy sheet for automotive panels in T4 temper, J. Mater. Metall. 9(2010) 137-142.

[26] H.H. Xu, Z.Q. Zhang, S.N. Wu, G.J. Huang, Effect of pre-straining and pre-ageing on bake hardening response of Al-Mg-Si alloy, Chin. J. Nonferrous. Met. 23(2013) 623-627.