Response of Cold Sprayed Ti6Al4V Coatings to Solid Particle Erosion and Micro-Scratch Wear Processes

Abstract:

Ti6Al4V alloy is widely used for aeronautical components due to a special combination of high mechanical properties, low density and good corrosion resistance at high temperature. These components are usually damaged by particles impacts during their operating time. When the reliability of these components is compromised, they are replaced with the consequent cost of material and time. Spraying coatings on the damaged surface could reveal as an alternative process to repair these components, increasing their operating life. Traditionally, thermal spray processes are used to repair the aeronautical components. However, the coatings produced by these processes are characterized by high residual stresses, porosity and oxidation. The cold spray technique is revealed as a promising spraying alternative due to the characteristic low temperature of the process. Consequently, residual stresses, oxidation, crack formation, phase transformations and microstructural changes are minimized. In this work, a cold spray technique was used to generate Ti6Al4V coatings onto a bulk of the same material. Three different spraying conditions were studied: Ti6Al4V coatings sprayed at 800oC; Ti6Al4V coatings sprayed at 1100oC; and Ti6Al4V coatings sprayed at 1100oC with a subsequent heat treatment: The wear resistance of these coatings was investigated by solid particle erosion and micro-scratch tests. The wear behaviour was determined under several wear tests conditions. Additionally, instrumented indentation tests were carried out on the coatings to determine their mechanical response. The wear mechanisms of the coatings were identified and compared to their microstructure and mechanical properties.

• Periodical: Materials Science Forum (Volume 941)
• Pages: 1680-1685
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.941.1680
• Online since: December 2018
• Authors: Miguel Ángel Garrido-Maneiro*, Paloma Sirvent, Daniel Elvira, Álvaro Rico, Claudio Munez, Pedro Poza
• Keywords: Cold Spray, Erosion, Instrumented Indentation, Micro-Scratch, Ti6Al4V Coatings

References

[1] R.R. Boyer, An Overview on the Use of Titanium in the Aerospace Industry, Mater Sci Eng A. 213 (1996) 103-114.

[2] H. Assadi, T. Schmidt, H. Richter, J.O. Kliemann, K. Binder, F. Gartner, T. Klassen, H. Kreye, On Parameter Selection in Cold Spraying, J Therm Spray Techn. 20 (2011) 1161-1176.

DOI: 10.1007/s11666-011-9662-9

[3] F.Gartner, T. Stoltenhoff, J. Voyer, H. Kreye, S. Riekehr, M. Kocak, Mechanical Properties of Cold-Sprayed and Thermally Sprayed Copper Coatings, Surf Coat Tech. 200 (2006) 6770-6782.

DOI: 10.1016/j.surfcoat.2005.10.007

[4] V.K. Champagne, The Cold Spray Deposition Process: Fundamentals and Applications, Woodhead Publishing Ltd, Cambridge, (2007).

[5] G. Bae, Y. Xiong, S. Kumar, K. Kang, C. Lee, General Aspects of Interface Bonding in Kinetic Sprayed Coatings, Acta Mater. 56 (2008) 4858-4868.

DOI: 10.1016/j.actamat.2008.06.003

[6] I. Finnie, D. H. McFadden, On the velocity dependence of the erosion of ductile metals by solid particles at low angles of incidence, Wear 48 (1978) 181-190.

DOI: 10.1016/0043-1648(78)90147-3

[7] W. C. Oliver, G. M. Pharr, An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J Mater Res. 7 (1992) 1564–1583.

DOI: 10.1557/jmr.1992.1564

[8] A. Zmitrowicz, Wear Patterns and Laws of Wear – A Review, J. Theor. Appl. Mech. 44 (2006) 219-253.

[9] ASTM. Standard Test Method for Conducting Erosion Tests by Solid Particle Impingement Using Gas Jets. ASTM G76-13.

DOI: 10.1520/g0076-04

[10] I.M. Hutchings, A model for the erosion of metals by spherical particles at normal incidence, Wear 70 (1981) 269-281.

DOI: 10.1016/0043-1648(81)90347-1