Effect of Cooling Condition after Warm Rolling on the Development of Microstructure and Texture in an ELC Steel

Abstract:

The microstructure and texture development in an extra low carbon steel during warm rolling (~ 80%) in a single pass at four different temperatures and at two different cooling conditions were studied. The g fibre texture develops at lower warm rolling temperatures (500 °C and 600 °C) and a very weak a fibre develops at higher rolling temperatures (700 °C and 800 °C). Very little or no difference in microstructure and texture development was observed under two cooling conditions at four rolling temperatures. No significant effect of cooling rates could be found at higher temperatures of rolling due to very fast static recrystallisation after rolling which also caused the weakening of texture. On the other hand deformation bands produced at low temperatures rolling helped in forming strong g fibre textures.

• Periodical: Solid State Phenomena (Volume 105)
• Pages: 259-264
• DOI: https://doi.org/10.4028/www.scientific.net/SSP.105.259
• Online since: July 2005
• Authors: Arunansu Haldar, R.K. Ray, A.J. Khan
• Keywords: Deformation Band, Static Recrystallization, Warm Rolling, γ Fibre

References

[1] S. Mishra and C. Darman: Int. Met. Rev. 27(1982), p.307.

[2] W.B. Huchinson: Int. Met. Rev. 29(1984), p.25.

[3] R.K. Ray, J.J. Jonas and R.E. Hook: Int. Mater. Rev. 39(1994), p.129.

[4] B. Huchinson: Phil. Trans.R. Soc. London A, 357(1999), p.1471.

[5] T. Senuma, H. Yada, R. Shimizu and J. Harase: Acta Metall. Mater. 38(1990), p.2673.

[6] G.H. Akbari, C.M. Sellars and J.J. Whiteman: Acta Metall. Mater. 45(1997), p.5047.

[7] M. Barnett and J.J. Jonas: ISIJ Int. 37(1997), p.697, p.706.

[8] M. Barnett and J.J. Jonas: ISIJ Int. 39(1999), p.856.

[9] A. Haldar and R.K. Ray: Accepted for publication in Materials Science Engg. A.

[10] H.J. Bunge: Texture Analysis in Material Science, Butterworths, London (1982).

[11] B. Bay, N. Hansen, D.A. Hughes and D. Kuhlman-Wilsdorf: Acta Metall. Mater. 40(1992), p.205.

[12] K. Ushida, H. Ohsone and M. Abe: Proc. 6 th Int. Conf. Textures Materials (ICOTOM 6) (1981), p.829.

[13] A. Haldar, X. Huang, T. Leffers, N. Hansen and R.K. Ray: Acta Materialia, 52(2004), p.5418.

[14] N. Hansen and D.J. Jensen: Trans. R. Soc. London A, 357(1999), p.1447.