This was not contrary to the reduction of tensile strength.
The data in fig.2(c) were the impact strength of composites with different filler.
It can be shown that the impact strength of three composites reduced a few, which of composite filled by graphite reached to 87KJ/m 2, the minimum of the three data was up to 78KJ/m 2.

Therefore, a fit over the refractive index data was applied, based on the Cauchy formula: n = p+q/λ 2.
Ref[1] Ref[2] Tauc method (αhν) 2 method Egap,SiC [eV] 3.31 3.37±0.05 1.87* 2.98* Egap,AlN [eV] 6.42 6.14±0.06 3.59±0.2 4.96±0.24 b [eV] -6.36 -4.26±0.3 -4.97±0.7 -4.04±0.77 This might be attributed to a particularly strong reduction of the tail-states in the SiC rich region.
The corresponding fitting parameters found matched very well the literature data for the crystalline state.

However, the latter was judged to be representative of the typical material behaviour of Type 316H stainless steel and the creep property data associated with it are currently used in the R5 high temperature assessment for predicting the creep damage accumulated in the HAZ [5].
Impurity segregation of elements, such as phosphorous and sulphur, leads to a reduction in the cohesive energy of grain boundaries and thereby offer the potential to enhance the susceptibility to inter-granular fracture [7].
[5] British Energy Ltd., R66, AGR materials data handbook, Issue 5 (1999)

Our preliminary Crystal-TRIM [12] simulations (not shown here) predicted this damage reduction.
For better visibility, the data are drawn for both positive and negative tilt values.
For better visibility, the data are drawn for both positive and negative tilt values.

The numerical results calculated with the dynamic explicit solver (abaqus) coupled with the remeshing method have been compared with experimental data.
Van den Boogaard, Time reduction in implicit single point incremental sheet forming simulation by refinement-derefinement, I.
Habraken, Material data identification to model the single point incremental forming process, International Journal of Material Forming 3 (Suppl 1), doi: 10.1007/s12289-010-0933-7 (2010), pp. 979-982

Crystalline phases were identified using the International Center for Diffraction Data (ICDD) database.
The Rietveld method was used to refine the XRD data using the MAUD program.
The results demonstrated that the replacement of Fe3+ by Al3+ ions and the increase of heat treatment temperature cause a slight reduction in Ms, Mr and Hc, favoring the antiferromagnetic ordering of such systems.

So each child configuration model only includes the rational configuration data consistent with a specific customer group.
When configuring, we should choose one of these children nodes to replace the parent GM node based on the CRs and rules; ③ -Accessional‖, in consideration of data redundancy and maintenance, we suppose to build GPS model for BGP only.
The size and complexity of the problem will be of much reduction.

We can conclude the structure of carbon emissions cost,which is shown in Table 2: Table2:The structure of carbon emissions cost Structure Related factors Carbon emissions cost External cost（EC） Prevention costs（PC） Control of cost（COC） Plan cost（PLC） Appraisal cost（AC） Failure cost（FC） Internal cost（IC） Carbon content（CAC） Production value（PV） Industrial added value（IAV) Carbon consumption (CCO） Meanwhile,we establish the external cost and internal cost model for the following respectively: (2) (3) Cost estimation model of carbon emissions 3.1Put forward the concept of carbon emissions currency cost We conduct analysis and Research on the cost of carbon emissions is to enable enterprises to make the accounting of carbon emissions cost more accurate and more clearly.Energy saving and emission reduction are the trend of the world economy,the high-speed development of Chinese
As a result of length reason,this paper analysis unit resources carbon monetary cost from the perspective of qualitative rather than from a quantitative point to data of empirical research.In future research,based on the model of carbon emissions currency cost drawn from this paper,we may collect related data to carry out empirical analysis,and then make the conclusion in this paper is more accurate so that it can better play the role of guidance and reference to the economics.

Few works have been published about the formation conditions of disordered solid solutions CoxPd1-x and there is no data on their magnetic properties both in bulk samples and in thin films.
This is in agreement with XRD data, which didn't show the formation of compounds on the interface between palladium and cobalt.
The X-ray pattern of Pd/hcp-Co(110) bilayers, after annealing at 500 °C, shows a reduction of the hcp-Co(110) peak and a formation of a new, strong (110) CoPd peak (Fig. 1a).

The in vitro release data is fitted into the different models such as zero order, first order, Higuchi and Peppa’s to understand the order of reaction and release mechanism.
This could cause a decrease in the effective diffusion co-efficient of the drug and therefore reduction in the drug release rate.
In order to elucidate model and mechanism of drug release, the in vitro data was transformed and interpreted at graphical interface constructed using various models.