Papers by Author: Mustapha Benachour

Abstract: In this paper, effect of stress ratio was investigated on macro and micro of fatigue crack growth rates (FCGRs) of Al-alloy 2024 T351. Microscopic fatigue crack growth rate present a change of slope with respect to the macroscopic fatigue crack growth rate. In addition, an increasing in stress ratio increases the fatigue life. Fractographic examination showed the presence of striations in Paris domain and secondary cracks at grain boundaries.

Abstract: The purpose of this paper is to estimate the number of cycles for fatigue crack initiation in notched plate under constant amplitude loading through tensile residual stress field of Aluminum alloy plate. Residual stress field was generated by plastic deformation using finite element method. Simulation of fatigue behavior was made on AFGROW code. It was shown that the fatigue crack initiation and propagation were affected by level of residual stress filed. In this investigation, the presence of tensile residual stresses reduces considerably the total fatigue life. Loading parameter namely stress ratio was studied. The decreasing in this parameter reduces the fatigue crack growth rate (FCGRs).