Microstructural Evolution of Compacted Graphite Iron under Thermo-Mechanical Fatigue Conditions

Abstract:

Cast iron components in combustion engines, such as cylinder blocks and heads, are exposed for long periods of time to elevated temperatures and subjected to large numbers of heating and cooling cycles. In complex components, these cycles can lead to localized cracking due to stresses that develop as a result of thermal gradients and thermal mismatch. This phenomenon is known as Thermo-Mechanical Fatigue (TMF). Compacted Graphite Iron (CGI) provides a suitable combination of thermal and mechanical properties to satisfy the performance of engine components. However, TMF conditions cause microstructural changes, accompanied by the formation of oxides at and close to the surface, which together lead to a growth in size of the cast iron. These microstructural changes affect the mechanical properties and accordingly the thermo-mechanical fatigue properties. The aim of this research is to provide insight into the microstructure evolution of CGI, with its complex morphology, under TMF conditions. For this, optical and scanning electron microscopy observations are made after cyclic exposure to air at high temperature, both without and with mechanical loading. It was found that the oxide layers, which develop at elevated temperatures, crack during the cooling cycle of TMF. The cracking results from tensile stresses developing during the cooling cycle. Therefore, paths for easy access of oxygen into the material are formed. Fatigue cracks that develop also show oxidation at their flanks. In order to quantify the oxide layers surrounding the graphite particles, Energy Dispersive X-Ray Analysis (SEM-EDX) and Electron Probe Micro Analysis (EPMA) are used.

• Periodical: Advanced Materials Research (Volume 409)
• Pages: 757-762
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.409.757
• Online since: November 2011
• Authors: S. Ghodrat, M. Janssen, Roumen H. Petrov, Leo A.I. Kestens, Jilt Sietsma
• Keywords: Compacted Graphite Iron, Growth, Oxidation, Thermo-Mechanical Fatigue (TMF)

References

[1] R. Hallstein, K.H. Lang, D. Löhe, E. Macherauch, Thermal-Mechanical Fatigue Behaviour of Vermicular Cast Iron, Crack Growth and Analysis, ICM8 Vol I. 6, p.301–306 (1999).

[2] ASM Metals Handbook, Volume 19, Fatigue and Fracture. ASM International, United States of America (1996).

[3] C. Halászi, C. Gaier, H. Dannbauer, Fatigue Life Prediction of Thermo-Mechanically Loaded Engine Component, MAGNA Powertrain, Engineering Center Steyr GmbH & Co. KG, Technical Report, Austria (2007).

[4] D. Löhe, T. Beck, K.H. Lang, Important Aspects of Cyclic Deformation, Damage and Lifetime Behaviour in Thermo-Mechanical Fatigue of Engineering Alloys. Fifth International Conference on Low Cycle Fatigue, (Eds. ): Portella P.D., Sehitoglu H., Hatanaka K., LCF5. DVM, Berlin, p.161–175 (2004).

[5] H.D. Merchant, Oxidation Kinetics of Iron-carbon Base Alloys, Oxid. Met., Vol. 2, No. 2, p.145–153 (1970).

DOI: 10.1007/bf00603653

[6] D. Jedrzejczyk, M. Hajduga, R. Lorek, High Temperature Oxidation as the Method of Surface Treatment of Cast Iron , METAL 2008, Hradec nad Moravici, Ceska republika, 13–15 May (2008).

[7] J.R. Davis (Ed. ), Cast irons. ASM Specialty Handbook, ASM International, Materials Park, OH 44073-0002, p.407–413 (1996).

[8] S.Y. Buni, N. Raman, S. Seshan, Sadhana, 29(1), p.117–127 (2004).

[9] K.R. Ziegler, J.F. Wallace, The Effect of Matrix Structure and Alloying on the Properties of Compacted Graphite Iron, AFS Transactions, 92, p.735–748 (1984).

[10] K. Roehrig, Thermal Fatigue of Gray and Ductile Cast Irons, AFS Transactions, 78-02, p.75–88 (1978).

[11] D.G. White, L. I. M., A. C. T., Growth and Scaling Characteristics of Cast Irons with Undercooled and Normal Flake Graphite, BCIRA Journal, 11(Report 689), p.223–230 (1963).

[12] C.F. Walton, T.J. Oper (Eds. ), Text Book, Iron Casting Handbook, Published by Iron castings society, Cleveland, Ohio (1981).