The Effect of Thiourea Additive to Elimination of the Iron Dissolved in Flux Solution of Hot Dip Galvanizing Process

Abstract:

Hot dip galvanizing is being widely used to the numerous constructional steels such as a guard rail of high way, various types of structural steel for manufacturing ship and for some other fields etc.. Recently, the cost of zinc is getting higher and higher, thus, a proper manufacturing process should be developed possibly to reduce the cost of production. one of hot dip galvanizing process, that is, flux solution immersion process is very important to control more effective coating. However, flux solution is deteriorated with increasing its using time because dissolved iron from structural steel due to continuous flux treatment was increasingly increased, which is resulted in coating badness and increment of dross. In this study, the effect of additives to elimination of iron dissolved in flux solution was investigated with four types of inner solution, that is, solution of inner barrel was filled with seawater, NaOH, NH4Cl, including parameters of amounts of thiourea(0.2,0.4 ,0.6 and 0.8g) and electrolysis experiment was carried out with applied current density at 20mA/cm2. The best effect for elimination of iron from flux solution is considered that inner barrel with separator should be filled with solution different from original flux solution which contained in iron ion, that is, its inner solution should be composed with seawater added with additives such as thiourea(0.4g), NaOH(0.2 g) and NH4Cl(10g). In particular, we can see that the optimum amount of thiourea to extract effectively iron from flux solution is 0.4g.

• Periodical: Advanced Materials Research (Volumes 538-541)
• Pages: 186-189
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.538-541.186
• Online since: June 2012
• Authors: Kyung Man Moon, Min Seok Oh, Jong Pil Won, Myung Hoon Lee, Yun Hae Kim
• Keywords: Dross, Electrolysis, Flux Solution, Hot Dip Galvanizing, Insoluble Anode, Thiourea

References

[1] B. H. Jung, M. G. Kim : J. of Kor. Soc. of Mar. Eng. Vol. 30, No. 6 (2006), p.709

[2] S. J. Kim, J. Y. Ko : J. of Kor. Soc. of Mar. Eng. Vol. 30, No. 6( 2006), p.57

[3] D. H. Youn, M. H. Lee, K. J. Kim, K. M. Moon : J. of Kor. Soc. of Mar. Eng. Vol. 29, No. 5 (2005), p.495

[4] Denny A. Jones, in : PRINCIPLES AND PREVENTION OF CORROSION, Maxwell Macmillian International Publishing Group, New York, USA, (1991), p.398

[5] The Techonlogy Center of the Coastal Development, in: Corrosion Control Manual of Harbor Steel Structure, Tokyo, Jappen, (1987), p.21

[6] W. Von Baeckmann, in: Handbook of CATHODIC CORROSION PROTECTION, Guef publishing Company, Houston Texas, USA, (1997), p.180

[7] Mars G. Fontana etc., in: Corrosion Engineering, McGraw-Hill, Inc,New Jersey, USA, (1978), p.39

[8] J.O.M. Bockris, K.N Reddy : Modern Electrochemistry,2, Appenum, Resetta Edition,(1977), p.1233

[9] R.M. Latanison, M.Kurrela, Corrosion, 39 , (1983) , p.179