Deposition and Tribological Properties of CVD Diamond/Diamond-Like Carbon Composite Films

Abstract:

The CVD diamond/diamond-like carbon composite film is fabricated on the WC-Co substrate by depositing a layer of Diamond-like Carbon film on the surface of conventional Micro- or Nano-crystalline diamond film. The hot filament chemical vapor deposition (HFCVD) method and vacuum arc discharge with a graphite cathode are adopted respectively to deposit the MCD/NCD and DLC films. A variety of characterization techniques, including filed emission scanning electron microscope (FE-SEM) and Raman spectroscopy are employed to investigate the surface morphology and atomic bonding state of as-deposited MCD/DLC and NCD/DLC composite film. The results show that both MCD/DLC and NCD/DLC composite films present similar surface morphology with the MCD and NCD films, except for scattering a considerable amount of small-sized diamond crystallites among the grain boundary area. The atomic-bonding state of as-deposited MCD/DLC and NCD/DLC composite films is determined by the top-layered DLC film, which is mainly consisted of amorphous carbon phase and no discernible sp3 characteristic peak can be observed from their Raman spectrum. Furthermore, the tribological properties of as-deposited MCD/DLC and NCD/DLC composite films is examined using a ball-on-plate reciprocating friction tester under both dry sliding and water-lubricating conditions, comparing with conventional DLC, MCD and NCD films. Silicon nitride balls are used as counterpart materials. For the CVD diamond/DLC composite films, the self-lubricating effect of top-layered DLC film is beneficial for suppressing the initial friction peak, as well as shortening the run-in period. The average friction coefficients of MCD/DLC and NCD/DLC composite films during stable sliding period are 0.07 and 0.10 respectively in dry sliding; while under water-lubricating condition, they further decreases to 0.03 and 0.07.

• Periodical: Advanced Materials Research (Volume 565)
• Pages: 615-620
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.565.615
• Online since: September 2012
• Authors: Bin Shen, Liang Wang, Su Lin Chen, Fang Hong Sun
• Keywords: CVD Diamond/DLC Composite Film, HFCVD, Tribological Property, Vacuum Arc Discharge

References

[1] X. C. Chen, Z. J. Peng, X. A. Yu, Z. Q. Fu, W. Yue and C. B. Wang: Appl. Surf. Sci. Vol. 257(8) (2011), p.3180.

[2] S. Ferreira, P. Duarte, F. A. Almeida and R. F. Silva: Diam. Relat. Mat. Vol. 20(4) (2011), p.464.

[3] R. Polini: Thin Solid Films Vol. 515(1) (2006), p.4.

[4] S. Prawer and R. J. Nemanich: Philos. Trans. R. Soc. Lond. Ser. A-Math. Phys. Eng. Sci. Vol. 362(1824) (2004), p.2537.

[5] R. Pfeiffer, H. Kuzmany, P. Knoll, S. Bokova, N. Salk and B. Gunther: Diamond and Related Materials Vol. 12(3-7) (2003), p.268.

DOI: 10.1016/s0925-9635(02)00336-9