Defect and Diffusion Forum
Vols. 261-262
Vols. 261-262
Defect and Diffusion Forum
Vols. 258-260
Vols. 258-260
Defect and Diffusion Forum
Vols. 254-257
Vols. 254-257
Defect and Diffusion Forum
Vol. 253
Vol. 253
Defect and Diffusion Forum
Vols. 251-252
Vols. 251-252
Defect and Diffusion Forum
Vol. 250
Vol. 250
Defect and Diffusion Forum
Vol. 249
Vol. 249
Defect and Diffusion Forum
Vols. 247-248
Vols. 247-248
Defect and Diffusion Forum
Vols. 245-246
Vols. 245-246
Defect and Diffusion Forum
Vols. 242-244
Vols. 242-244
Defect and Diffusion Forum
Vol. 241
Vol. 241
Defect and Diffusion Forum
Vols. 237-240
Vols. 237-240
Defect and Diffusion Forum
Vols. 235-236
Vols. 235-236
Defect and Diffusion Forum Vol. 249
Paper Title Page
Abstract: The dielectric breakdown strengths of two series of sintered alumina samples of low and high impurity content (where Si is the dominant element with, respectively, 90 and 1500 ppm) and impurity level (25 ppm of Si and 12 ppm of Ti) are compared with positron lifetime measurements. The dielectric breakdown strength of sintered alumina is found higher than that of single crystal. This improvement is stronger when silicon is the only major foreign element. If, in addition to SiO2, MgO and CaO are present in substantial amounts, the improvement is lessened. This is attributed to the enhanced bulk solubility of Si. These results are discussed by calling for the potential traps for positrons and electrons that are located at grain boundaries. It is deduced that the improvement of the dielectric breakdown strength stems from the
consequences of Si segregation at grain boundaries via electron trapping in shallow traps, which are likely the x '' Al • Al ) V : (3Si clusters.