Surface Modification of Pure Magnesium and Magnesium Alloy AZ91 by Friction Stir Processing

Article Preview

Abstract:

In recent years an interest in magnesium and magnesium alloys not only for the automotive industry but also for medical applications was increasing due to the low density and good specific strength. Magnesium alloys show good castability but lower ductility and strength than wrought materials. For this reason, refinement of grains and homogenous distribution of intermetallic phases are needed to improve formability and mechanical properties. On the other hand, the degradation of the material by corrosion is influenced by the grain size and phase distribution. This work investigates the microstructure evolution of pure Mg and magnesium alloy AZ91 by friction stir processing (FSP) technique. FSP experiments are carried out by constant force, optimizing the rotation and feed rate to obtain a homogenous microstructure, free of defects stir zone, good surface finishing and stable conditions during the process. The results show that the grain size is affected by the spindle speed. Increasing the number of passes reduces also the size of the grains and the intermetallic phases in the AZ91 alloy. The overlapping of passes between overlapping ratio 0.5 to 1 determines an uniform depth of the stir zone over a larger surface area.Hardness measurements are performed to evaluate the influence of FSP parameters on the mechanical properties. The degradation rate of the studied FSP Mg alloys is determined by hydrogen evolution in corrosion immersion tests, which depend strongly on the phase distribution and grain size.

You might also be interested in these eBooks

Info:

Periodical:

Key Engineering Materials (Volumes 651-653)

Pages:

796-801

Citation:

Online since:

July 2015

Export:

Price:

Permissions CCC:

Permissions PLS:

Сopyright:

© 2015 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

* - Corresponding Author

[1] B. Mordike, T. Ebert: Magnesium: Properties-applications-potential, Materials Science and Engineering: A, Vol. 302, (2001), 37-45.

Google Scholar

[2] M. P. Staiger, A. M. Pietak, J. Huadmai, G. Dias: Magnesium and its alloys as orthopedic biomaterials: A review, Biomaterials 27, (2006), 1728–1734.

DOI: 10.1016/j.biomaterials.2005.10.003

Google Scholar

[3] J. Gandra, R. M. Miranda, P. Vilaca: Effect of overlapping direction in multipass friction stir processing, Materials Science and Engineering A, Vol. 528, (2011), 5593-5599.

DOI: 10.1016/j.msea.2011.03.105

Google Scholar

[4] A. A. Nia, H. Omidvar, S. H. Nourbakhsh: Effects of overlapping multi-pass friction stir process and process and rapid cooling on the mechanical properties and microstructure of AZ31 magnesium alloy, Materials and Design, Vol. 58, (2014), 298-304.

DOI: 10.1016/j.matdes.2014.01.069

Google Scholar

[5] M. Alvaro-Lopez, M. D. Pereda, J. A. del Vallea, M. Fernandez-Lorenzo, M. C. Garcia-Alonso, O. A. Ruano and M. L. Escudero: Corrosion behaviour of AZ31 magnesium alloy with different grain sizes in simulated biological fluids, (2009).

DOI: 10.1016/j.actbio.2009.04.041

Google Scholar

[6] M. B. Kannan, W. Dietzel, R. Zettler: In vitro degradation behaviour of a friction stir processed magnesium alloy, J Mater Sci: Mater Med, Vol. 22, (2011), 2397-2399.

DOI: 10.1007/s10856-011-4429-x

Google Scholar

[7] M. -C. Zhao, M. Liu, G. Song, A. Atrens: Influence of the β-phase morphology on the corrosion of the Mg alloy AZ91, Corrosion Science, Vol. 50, (2008), 1939-(1940).

DOI: 10.1016/j.corsci.2008.04.010

Google Scholar

[8] Datasheet of the material provided by the manufacturer Non Ferrum Metal Powders, (2013).

Google Scholar

[9] G. Song, A. Atrens, D. StJohn: An Hydrogen Evolution Method for the Estimation of the Corrosion Rate of Magnesium Alloys, Magnesium Technology 2001, (2001), 256-257.

DOI: 10.1002/9781118805497.ch44

Google Scholar

[10] R. Ambat, N. N. Aung, W. Zhou: Evaluation of microstructural effects on corrosion behavior of AZ91D magnesium alloy, Corrosion Science, Vol. 42, (2000), 1439-1450.

DOI: 10.1016/s0010-938x(99)00143-2

Google Scholar