Wetting and Interfacial Behavior of Molten Al on Mo-Ni(Co)-Si Coated SiC Ceramic

San Tuan Zhao; Xiang Zhao Zhang; Gui Wu Liu; Hong Yan Xia; Zhong Qi Shi; Guan Jun Qiao

doi:10.4028/www.scientific.net/KEM.697.481

Paper Titles

Preparation and Properties of Si₃N₄-SiC Radar Wave-Absorbing Nanocomposites
p.462

Preparation of Sialon/Si₃N₄-SiC Composite Refractories Using Kyanite Tailings
p.467

Study on the Cause and Control of Defects on Process of CVD SiC
p.472

Fabrication of Mullite Coating and its Oxidation Protection for Carbon Fiber Reinforced SiC Composites
p.476

Wetting and Interfacial Behavior of Molten Al on Mo-Ni(Co)-Si Coated SiC Ceramic
p.481

Effect of Additives on Bond Property for Phenolic Resin-Based Adhesive
p.485

Preparation and Properties of SiC/Si-B-C-N Ceramic Composites
p.489

Preparation of B₄C-ZrB₂ Laminated Composites by Non-Aqueous Tape Casting and Hot-Press Sintering
p.494

Structural-Functional Integrative Mullite_f/SiBN Composites with Excellent Wave-Transparent and Mechanical Properties
p.498

HomeKey Engineering MaterialsKey Engineering Materials Vol. 697Wetting and Interfacial Behavior of Molten Al on...

Wetting and Interfacial Behavior of Molten Al on Mo-Ni(Co)-Si Coated SiC Ceramic

Abstract:

The Mo-Ni (Co)-Si metallizing coatings on the SiC ceramic substrate were prepared by vacuum cladding process. The wetting and spreading of molten Al on coated SiC ceramic substrates at 900 oC were investigated by the sessile drop technique, and the interfacial behavior of the Al/coated SiC wetting couples was analyzed. The experimental results showed that the final contact angle of Al/M20NiSi coated SiC was close to 0o. With the increase of Mo content in the Mo-Ni-Si coating, the shape of the sessile drop became very irregular due to the strong interactions between the Al drop and the coating, so it was unable to precisely characterize the contact angles of Al/Mo30NiSi and Al/Mo40NiSi systems. The final contact angle of Al/Mo10CoSi coated SiC system was also close to 0o, however, the final contact angle of Al/Mo20CoSi coated SiC system climbed to ~42o with the Mo content increasing from 10 at.% to 20 at.%. The significant increase of contact angle may be caused by the accumulation of Mo near the triple line which can impede the spreading of Al drop.