Morphology of Carbon Micro-Coils

M. Fujii; S. Motojima

doi:10.4028/www.scientific.net/MSF.449-452.205

Paper Titles

Prediction of Microstructure During High Temperature Forming of Ti-6Al-4V Alloy
p.189

Surface Amorphization in Intermetallic Compounds by Shot Peening
p.197

Combustion Synthesis Process of Ag Added Al₃Ti Intermetallic Compound
p.201

Morphology of Carbon Micro-Coils
p.205

Synthesis of Porous Mullite by Vapor Phase Reaction
p.209

Self-Propagating High-Temperature Synthesis of Aluminum Nitride and its Characterization
p.213

Fabrication of Activated Carbon Fibers from Stabilized PAN-Based Fibers by KOH
p.217

Role of Unstable Chemical Species (Non-Graphitic Carbon and Flowing NH₃ Gas) on the Equilibrium Point of the Reaction Product (Carbide, Carbo-Nitride or Nitride)
p.221

HomeMaterials Science ForumMaterials Science Forum Vols. 449-452Morphology of Carbon Micro-Coils

Morphology of Carbon Micro-Coils

Abstract:

The double helical carbon micro-coils were obtained by chemical vapor deposition. As-grown carbon micro-coils with amorphous structure were heat-treated at various temperatures up to 3000°C . By heat treatment, the shape of the coils was not changed. The morphology of these coils was observed in detail using electron microscope. The lattice structure was analyzed by X-ray diffraction method. Heat treatment temperature dependence of the magnetoresistance and the measurement of Raman spectra suggest that the coils heattreated at higher temperature are more highly graphitized.