Influence of Li Additions on the Microstructure and Corrosion Response of 2XXX Series Aluminium Alloys

Abstract:

This paper discusses two Al-Cu alloys for aerospace applications, one of which has an addition of between 1.6 and 2.0 wt.% of Li. The alloys are AA2024-T3 (Al-Cu) and AA2099-T8E77 (Al-Cu-Li). Microstructural analysis via Field Emission Gun Transmission Electron Microscope (FEGTEM) and Field Emission Gun Scanning Electron Microscope (FEGSEM) utilising Energy Dispersive Spectroscopy (EDS) and Electron Backscatter Detector (EBSD) techniques have been used to characterise the two microstructures and phases contained within them. Anodic polarisation and immersion testing in a 3.5 wt.% NaCl solution have been carried out and a comparison of the corrosion mechanisms has been made. AA2024-T3 had a fine, equiaxed grain structure, whereas AA2099-T8E77 had a substantial amount of recrystallized grains. Finer grains were also observed on AA2099-T8E77, however, the vast majority were larger than the maximum detection limit of the EBSD technique. Intergranular and pitting corrosion were observed on both alloys following immersion testing, however, the intergranular corrosion (IGC) was more prominent on AA2099-T8E77. Anodic polarisation indicated that AA2024-T3 was more noble, highlighting that the Li-containing AA2099-T8E77 alloy was more susceptible to corrosion. The T₁ (Al₂CuLi) phase within AA2099-T8E77 was seen to be highly active following immersion and anodic polarisation tests. The corrosion pits on AA2099-T8E77 were seen to propagate to a depth of ~ 80 to 100 μm, with a maximum of 126 μm recorded. For AA2024-T3 the maximum depth recorded was 77 μm and the average depth was between 60 and 70 μm.

• Periodical: Materials Science Forum (Volumes 794-796)
• Pages: 193-198
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.794-796.193
• Online since: June 2014
• Authors: David M. Carrick*, Simon C. Hogg, Geoffrey D. Wilcox
• Keywords: Aluminium Alloy, Anodic Polarisation, Copper, Corrosion, Immersion Testing, Lithium

References

[1] C. Giummarra, B. Thomas, and R. J. Rioja, New Aluminium Lithium Alloys for Aerospace Applications, in Proceedings of the Light Metals Technology Conference, Saint-Sauveur, Quebec, Canada, (2007).

[2] N. R. Council, New Materials for Next-Generation Commercial Transports. National Academics Press, (1996).

[3] P. Niskanen, T. H. Sanders, J. G. Rinker, and M. Marek, Corrosion of Aluminium Alloys containing Lithium, Corros. Sci., vol. 22, no. 4, p.283 – 304, (1982).

DOI: 10.1016/0010-938x(82)90031-2

[4] Z. Huang and M. H. Loretto, Influence of Lithium additions on precipitation and Age Hardening of 7075 alloy, Mater. Sci. Technol., vol. 9, p.967–980, (1993).

DOI: 10.1179/mst.1993.9.11.967

[5] Y. Ma, X. Zhou, G. E. Thompson, T. Hashimoto, P. Thomson, and M. Fowles, Distribution of Intermetallics in an AA 2099-T8 Aluminium Alloy extrusion, Mater. Chem. Phys., vol. 126, no. 1–2, p.46–53, Mar. (2011).

DOI: 10.1016/j.matchemphys.2010.12.014

[6] I. J. Polmear, Light Alloys: Metallurgy of the Light Metals, Second Edi. Edward Arnold Publishing, (1989).

[7] S. Adhikari and K. R. Hebert, Factors controlling the time evolution of the corrosion potential of Aluminum in alkaline solutions, Corros. Sci., vol. 50, no. 5, p.1414–1421, (2008).

DOI: 10.1016/j.corsci.2008.01.001

[8] H. Ezuber, A. El-Houd, and F. El-Shawesh, A study on the corrosion behavior of Aluminum Alloys in seawater, Mater. Des., vol. 29, p.801–805, (2008).

DOI: 10.1016/j.matdes.2007.01.021

[9] N. Birbilis and R. G. Buchheit, Electrochemical Characteristics of Intermetallic Phases in Aluminum Alloys An Experimental Survey and Discussion, J. Electrochem. Soc., vol. 152, no. 4, p.140–151, (2005).

DOI: 10.1149/1.1869984

[10] W. Da Ren, J. Li, Z. Zheng, and W. Chen, Localized corrosion mechanism associated with precipitates containing Mg in Al alloys, Trans. Nonferrous Met. Soc. China, vol. 17, p.727–732, (2007).

DOI: 10.1016/s1003-6326(07)60164-2

[11] W. R. and Z. Z. Jin-feng Li, Wen-jing Chen, Xu-shan Zhao, Corrosion behavior of 2195 and 1420 A1-Li alloys in neutral 3. 5% NaCl solution under tensile stress, Trans. Nonferrous Met. Soc. China, vol. 16, p.1171–1177, (2006).

DOI: 10.1016/s1003-6326(06)60396-8

[12] J. F. Li, C. X. Li, Z. W. Peng, W. J. Chen, and Z. Q. Zheng, Corrosion mechanism associated with T1 and T2 precipitates of Al–Cu–Li alloys in NaCl solution, J. Alloys Compd., vol. 460, no. 1–2, p.688–693, Jul. (2008).

DOI: 10.1016/j.jallcom.2007.06.072

[13] N. Metals, Simulation on function mechanism of T 1 (Al2CuLi) precipitate in localized corrosion of Al-Cu-Li alloys, no. 50401012, (2006).

[14] I. J. Polmear, Aluminium Alloys – A Century of Age Hardening, Mater. Forum, vol. 28, p.1–14, (2004).

[15] Z. Szklarska-Smialowska, Pitting corrosion of Aluminum, Corros. Sci., vol. 41, p.1743–1767, (1999).

DOI: 10.1016/s0010-938x(99)00012-8

[16] C. Henon and S. Rouault, Comparison of corrosion performance and mechanisms of Al-Cu alloys with and without Li addition ., in ICAA13: 13th International Conference on Aluminum Alloys, Pittsburgh, Pennysylvania, USA, (2013).

DOI: 10.1002/9781118495292.ch63

[17] ALCOA, Alloy 2024 Sheet and Plate, 2005. [Online]. Available: http: /www. alcoa. com/mill_products/catalog/pdf/alloy2024techsheet. pdf. [Accessed: 21-Jan-2013].

[18] ALCOA, Alloy 2099-T83 and 2099-T8E67 Extrusions, 2005. [Online]. Available: http: /www. alcoa. com/adip/catalog/pdf/Alloy2099TechSheet. pdf. [Accessed: 21-Jan-2013].

DOI: 10.31399/asm.ad.al0422

[19] C. Vargel, Corrosion of Aluminium. Elsevier Science, (2004).