Influence of Reinforcement Geometry on the Very High-Cycle Fatigue Behavior of Aluminium-Matrix-Composites

Abstract:

During technical operation, high performance materials are partially exposed to high frequency cyclic loading conditions. Furthermore, the small strains in the very high cycle fatigue (VHCF)-regime lead to accumulative damage which causes crack initiation related to an appropriate local deformation leading to final fatal fracture. At the same time, quite high requirements with regard to high number of cycles without any damage are demanded for many applications. Fields of application of these light-weight, but expensive materials, are e.g. in the automobile industry (e.g. engine blocks, cylinder heads, brakes).The fatigue behavior of Al-matrix composites (Al-MMCs) reinforced by alumina particles (15 vol.% Al2O3) or short fibers (20 vol.% Saffil), respectively, was already intensively studied in the LCF and HCF range. The present study is focusing on investigations in the very high cycle fatigue regime at stress amplitudes up to 140 MPa to reach fatigue life of about 1010 cycles. All experiments were carried out using an ultrasonic fatigue testing device under symmetric loading conditions (R=-1). Fatigue tests were accompanied by in situ thermography measurements to record the temperature of the whole specimen and to find “hot spots” indicating changes in microstructure and therefore the initiation or growth of cracks. Moreover, the resonant frequency as well as the damage parameter were evaluated to determine the beginning of damage. For a better understanding of the damage mechanism (matrix decohesion, matrix failure or failure of reinforcement) all fractured surfaces were investigated by scanning electron microscopy. The combination of these methods contributes to a better understanding of the underlying mechanism of damage in aluminum-matrix-composites.

• Periodical: Materials Science Forum (Volumes 825-826)
• Pages: 150-157
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.825-826.150
• Online since: July 2015
• Authors: Alexandra Müller*, Anja Weidner, Horst Biermann
• Keywords: Aluminium-Matrix-Composites, Thermography, Ultrasonic Fatigue Testing, Very High Cycle Fatigue

References

[1] K.U. Kainer, Metallische Verbundwerkstoffe, Wiley-VCH Verlag GmbH, Weinheim, (2003).

[2] L.F. Coffin Jr., A Study of the Effects of Cyclic Thermal Stress on a Ductile Metal, Trans. ASME. 76 (1954) 931-950.

DOI: 10.1115/1.4015021

[3] O. Hartmann, Einfluß der Matrix und der Form der Verstärkungen von Metallmatrix-Verbundwerkstoffen auf deren zyklisches Verformungsverhalten zwischen -100°C und 300°C, Ph.D. Thesis, Universität Erlangen-Nürnberg, (2002).

[4] M. Papakyriacou, H.R. Mayer, S.E. Stanzl-Tschegg, M. Gröschl, Fatigue properties of Al2O3-particle-reinforced 6061 aluminium alloy in the high-cycle regime, Int. J. Fatigue 18 (1996) 475-481.

DOI: 10.1016/0142-1123(96)00090-4

[5] A.R. Vaidya, J.J. Lewandowski, Effects of SiCp size and volume fraction on the high cycle fatigue behavior of AZ91D magnesium alloy composites, Mat. Sci. Eng. A 220 (1996) 85-92.

DOI: 10.1016/s0921-5093(96)10464-0

[6] C. Li, F. Ellyin, Fatigue damage and its localization in particulate metal matrix composites, Mat. Sci. Eng. A 214 (1996) 115-121.

DOI: 10.1016/s0142-1123(97)82580-7

[7] H. Mayer, M. Fitzka, R. Schuller, Constant and variable amplitude ultrasonic fatigue of 2024-T351 aluminium alloy at different load ratios, Ultrasonics 53 (2013) 1425-1432.

DOI: 10.1016/j.ultras.2013.02.012

[8] D. Krewerth, A. Weidner, H. Biermann, Application of in situ thermography for evaluating the high-cycle and very high-cycle fatigue behavior of cast aluminium alloy AlSi7Mg (T6), Ultrasonics 53 (2013) 1441-1449.

DOI: 10.1016/j.ultras.2013.03.001

[9] Y. Ochi, K. Masaki, T. Matsumura, M. Wadasako, Effects of volume fraction of alumina short fibers on high cycle fatigue properties of Al and Mg alloy composites, Mater. Sci. Eng. A 468-470 (2007) 230-236.

DOI: 10.1016/j.msea.2006.09.122

[10] J. Llorca, Fatigue of particle- and whisker-reinforced metal-matrix composites, Prog. Mater. Sci. 47 (2002) 283-353.

DOI: 10.1016/s0079-6425(00)00006-2

[11] N. Chawla, Y.L. Shen, Mechanical behavior of particle reinforced metal matrix composites, Adv. Eng. Mater. 3 (2001) 357-370.

DOI: 10.1002/1527-2648(200106)3:6<357::aid-adem357>3.0.co;2-i

[12] D. Krewerth, A. Weidner, H. Biermann, Fatigue crack initiation and damage mechanisms during ultrasonic fatigue testing of cast aluminium alloy AlSi7Mg, FDMD II (2014) 10005.

DOI: 10.1051/matecconf/20141210005