A Novel Way to Modify PTFE Membrane into Hydrophilicity

Abstract:

Polytetrafluoroethylene (PTFE) membrane, with high resistances to acid, alkali and other chemical corrosion, is the ideal filter material in water treatment, which can be used in a variety of harsh environment. However, the hydrophobictity of PTFE membrane limits its wide application in water treatment. Thus, the hydrophilic modification of PTFE membrane attracts much attention. In this work, the microporous PTFE membrane was treated by a novel strategy for enhancing its hydrophilicity. The pristine microporous PTFE membrane was modified by assembly of fluorocarbon surfactant. The structure and morphology of the membranes were characterized by attenuated Fourier Transform Infrared spectroscopy (ATR-FTIR) and scanning electron microscope (SEM). The variation of wettability was evaluated by the change of water contact angle (WCA). And the influences of the concentration of fluorocarbon surfactant and modification time on PTFE WCA were also investigated as well. The WCA of the pristine PTFE membrane is 156°. After modified by 5.0 g/L of fluorocarbon surfactants, the WCA reduced to 4.3°, indicating that the hydrophobic PTFE membrane was transformed into a hydrophilic one. FTIR and SEM results indicated that there were hydrophilic groups, such as carbonyl (-C=O) and hydroxyl (–OH) existing on the surface of PTFE membrane after modification. And WCA of the hydrophilic membrane showed a slight increase from 4.3°to 8° after a week, indicating that the hydrophilic PTFE membrane exhibiting a persistent durability.

• Periodical: Materials Science Forum (Volume 898)
• Pages: 1892-1895
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.898.1892
• Online since: June 2017
• Authors: Shi Jie Liu, Su Ping Cui, Zhen Ping Qin, Chua Jun Fei, Ya Li Wang, Hong Xia Guo*
• Keywords: Hydrophilicity, Modification, PTFE Membrane

References

[1] Wang S, Li J, Suo J, et al. Surface modification of porous poly(tetrafluoraethylene) film by a simple chemical oxidation treatment[J]. Applied Surface Science, 2010, 256(7): 2293-2298.

DOI: 10.1016/j.apsusc.2009.10.055

[2] Wang S, Li J, Suo J, et al. Surface modification of porous poly(tetrafluoraethylene) film by a simple chemical oxidation treatment[J]. Applied Surface Science, 2010, 256(7): 2293-2298.

DOI: 10.1016/j.apsusc.2009.10.055

[3] Sun H X, Zhang L, Chai H, et al. Surface modification of poly (tetrafluoroethylene) films via plasma treatment and graft copolymerization of acrylic acid[J]. Desalination, 2006, 192(1-3): 271-279.

DOI: 10.1016/j.desal.2005.07.038

[4] Wang C, Chen J R, Li R. Studies on surface modification of poly(tetrafluoroethylene) film by remote and direct Ar plasma[J]. Applied Surface Science, 2008, 254(254): 2882-2888.

DOI: 10.1016/j.apsusc.2007.10.029

[5] Tu C Y, Wang Y C, Li C L, et al. Expanded poly(tetrafluoroethylene) membrane surface modification using acetylene/nitrogen plasma treatment[J]. European Polymer Journal, 2005, 41(10): 2343-2353.

DOI: 10.1016/j.eurpolymj.2005.04.022

[6] Wang C, Chen J R. Studies on surface graft polymerization of acrylic acid onto PTFE film by remote argon plasma initiation[J]. Applied Surface Science, 2007, 10(10): 4599-4606.

DOI: 10.1016/j.apsusc.2006.10.014

[7] Hopp B, Smausz T, Kresz N, et al. Adhesion strength measurements of excimer-laser-treated PTFE surfaces using liquid photoreagents[J]. Proc Spie, 2003, 5131(11): 190-194.

DOI: 10.1117/12.513608

[8] Feng W, Li J, Zhu H, et al. Physical modification of polytetrafluoroethylene flat membrane by a simple heat setting process and membrane wetting remission in SGMD for desalination[J]. Desalination, 2014, 354(354): 143–152.

DOI: 10.1016/j.desal.2014.09.030

[9] Rychkov D, Yablokov M, Rychkov A. Chemical and physical surface modification of PTFE films—an approach to produce stable electrets[J]. Applied Physics A, 2012, 107(3): 589-596.

DOI: 10.1007/s00339-012-6834-5

[10] Noh J H, Hong K B, Noh I, et al. Surface modification of polytetrafluoroethylene using atmospheric pressure plasma jet for medical application[J]. Surface & Coatings Technology, 2007, 201(9–11): 5097-5101.

DOI: 10.1016/j.surfcoat.2006.07.223

[11] Lee S W, Hong J W, Wye M Y, et al. Surface modification and adhesion improvement of PTFE film by ion beam irradiation[J]. Nuclear Instruments & Methods in Physics Research, 2004, 219(1): 963-967.

DOI: 10.1016/j.nimb.2004.01.197

[12] Kato Y, Kanda K, Haruyama Y, et al. Surface modification of ptfe by synchrotron radiation under the O2 gas atmosphere[C]/ Microprocesses and Nanotechnology Conference, 2004. Digest of Papers. 2004 International. IEEE, 2004: 413–415.

DOI: 10.1109/imnc.2004.245648