Unique Effect of Carbon Addition on Development of Deformation and Recrystallization Textures in Heavily Cold-Rolled Fe-3%Si Alloys

Article Preview

Abstract:

This study investigated the effects of carbon addition on the development of deformation and recrystallization textures in 3 mass% Si steels cold-rolled by 95% reduction in thickness. A 3% Si steel with 0.016 mass% carbon developed RD // <110> (α-fiber) cold-rolling texture to a much greater extent than a 3% Si steel containing carbon less than 0.0005 mass%, whereas it is well known that the development of α-fiber rolling texture is suppressed by the addition of carbon in steels without silicon. This unique effect of carbon addition in the 3% Si steel appeared to be originated from a change in active slip systems. Straight slip bands were observed in the specimen without carbon, and the active slip plane was identified as {110}. On the other hand, wavy slip bands were observed in the steel containing carbon resulted from the activation of {112} and {123} slip planes in addition to {110}. It was also observed that {411}<148> recrystallization texture developed in the carbon-bearing 3% Si steel. Since the recrystallized grains with {411}<148> orientation preferentially nucleated in the vicinity of highly-strained deformation bands formed in deformed grains having α-fiber orientations, it is concluded that the development of {411}<148> recrystallization texture was resulted from the formation of the α-fiber texture after heavy cold-rolling in the carbon-bearing 3% Si steel.

You might also be interested in these eBooks

Info:

Periodical:

Pages:

890-895

Citation:

Online since:

December 2018

Export:

Price:

Permissions CCC:

Permissions PLS:

Сopyright:

© 2018 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

* - Corresponding Author

[1] Y. Hayakawa, J. A. Szpunar, Acta Mater. 45 (1997) 1285-1295.

Google Scholar

[2] T. Kumano, T. Haratani, Y. Ushigami, ISIJ Int. 43 (2003) 736-745.

Google Scholar

[3] M.Z. Quadir, B.J. Duggan, Acta Mater. 52 (2004) 4011-4021.

Google Scholar

[4] P. Gobernado, R.H. Petrov, D. Ruiz, L.A.I. Kestens, Scr. Mater. 66 (2012) 623-626.

Google Scholar

[5] M. Takenaka, Y. Shingaki, T. Imamura, Y. Hayakawa, Mater. Sci. Eng. 82 (2015) 012042.

Google Scholar

[6] H. Inagaki, ISIJ Int. 34 (1994) 313-321.

Google Scholar

[7] M. R. Barnett, L. Kestens, Textures and Microstructures, 34 (2000) 1-22.

Google Scholar

[8] S. Takeuchi, E. Furubayashi, T. Taoka, Acta Metall. 15 (1967) 1179-1191.

Google Scholar

[9] T. Taoka, E. Furubayashi, S. Takeuchi, Trans. ISIJ 6 (1966) 290-316.

Google Scholar