Search results
Online since: October 2011
Authors: Euler Araujo dos Santos, Vanessa Danielle de Oliveira Fortes, Wandeberg Aranha Diniz, Cristiane Xavier Resende, Luiz Eduardo Almeida, Zaine Teixeira
The minimum pH was kept at 10 by additions of KOH 0.1 mol L-1.
Fig. 1.
This sample also exhibited peaks at 406, 442 and 479 cm-1 assigned to n2 PO43- as well as at 1026, 1064 and 1081 assigned to n3 PO43- of b-TCP [13,15].
References [1] J.
Nanobiotech. 1 (2010) 42-49
Fig. 1.
This sample also exhibited peaks at 406, 442 and 479 cm-1 assigned to n2 PO43- as well as at 1026, 1064 and 1081 assigned to n3 PO43- of b-TCP [13,15].
References [1] J.
Nanobiotech. 1 (2010) 42-49
Hydrogen Storage, Microstructure and Mechanical Properties of Strained Mg65Ni20Cu5Y10 Metallic Glass
Online since: November 2012
Authors: Adam Revesz, Péter Szommer, Ágnes Kis-Tóth, Tony Spassov
ribbon
edge
center
Figure 1.
The average Vickers hardness of the ribbon is 479 HV, which values is considerably higher than that of a melt-spun Mg-Cu-Y alloy [23].
TÁMOP 4.2.1.
/B-09/1/KMR-2010-0003.
References [1] L.
The average Vickers hardness of the ribbon is 479 HV, which values is considerably higher than that of a melt-spun Mg-Cu-Y alloy [23].
TÁMOP 4.2.1.
/B-09/1/KMR-2010-0003.
References [1] L.
Online since: December 2014
Authors: Yong Hong Wan, Wei Li Xu, Zong Bin Huang
Fig. 1.
Table. 1 Thickness cases of patchwork HF part No.
For lightweight in solution 1, 1.02kg was decreased about 22% to the benchmarking car and 1.53kg decreased about 33.3% in solution 2.
References [1] Karbasian, H., Tekkaya, A.E., 2010.
SAE International Journal of Materials and Manufacturing 1 (1), 472–479
Table. 1 Thickness cases of patchwork HF part No.
For lightweight in solution 1, 1.02kg was decreased about 22% to the benchmarking car and 1.53kg decreased about 33.3% in solution 2.
References [1] Karbasian, H., Tekkaya, A.E., 2010.
SAE International Journal of Materials and Manufacturing 1 (1), 472–479
Online since: October 2014
Authors: Yue Ming Sun, Wei Jiang, Yu Dai, Bin Huang, Xin Xin Ban, Huan Ge Xu, Ya Ping Yang, Yuan Yuan Liu, Ya An Zhang
Scheme 1.
Fig. 1.
Their photoluminescence properties are presented in Table 1.
The results are shown in Table 1.
References [1] H.
Fig. 1.
Their photoluminescence properties are presented in Table 1.
The results are shown in Table 1.
References [1] H.
Online since: January 2021
Authors: Shi Liu, Sa Jian Wu, Yong Li Wang, Liang Yin Xiong, Jing Li
A final annealing treatment was carried out at 750 °C for 1 hour in vacuum.
The alloy composition is listed in Table 1 and the photograph of 14Cr ODS-FeCrAl cladding tubes is shown in Fig.1.
Table 1 Chemical compositiond of ODS-FeCrAl alloy (wt%).
References [1] B.
Mater. 479 (2016) 36-47
The alloy composition is listed in Table 1 and the photograph of 14Cr ODS-FeCrAl cladding tubes is shown in Fig.1.
Table 1 Chemical compositiond of ODS-FeCrAl alloy (wt%).
References [1] B.
Mater. 479 (2016) 36-47
Online since: March 2023
Authors: Arie Wibowo, Ade Wahyu Yusariarta, Gusti Umindya Nur Tajalla, Jane Ramadhani, Riska Rachmantyo
The HAp-Zn/SA was prepared with a certain ratio of PBS: Sample (1:1).
Fig. 1.
Table 1.
References [1] E.
Charact., vol. 62, no. 5, (2011) 469–479
Fig. 1.
Table 1.
References [1] E.
Charact., vol. 62, no. 5, (2011) 469–479
Online since: June 2017
Authors: Jian Hua Wu, Xiao Hui Huang, Ji Xue Zhou, Bai Chang Ma, Yuan Sheng Yang, Wei Hong Li, Jin Wang, Hai Hua Zhuang
Table 1 Forming parameters of the surface films on AZ91D alloy melt.
Fig. 2 EDS-spectra and compositions from (a) Outer layer, (b) Regular particle, (c) Irregular particle shown in Fig. 1(a) and (d) Surface shown in Fig. 1(b).
Conclusions 1.
References [1] Wang Xianfei, Xiong Shoumei, J.
Forum. 475-479 (2005) 2543-2546
Fig. 2 EDS-spectra and compositions from (a) Outer layer, (b) Regular particle, (c) Irregular particle shown in Fig. 1(a) and (d) Surface shown in Fig. 1(b).
Conclusions 1.
References [1] Wang Xianfei, Xiong Shoumei, J.
Forum. 475-479 (2005) 2543-2546
Online since: June 2012
Authors: Yu Hong Li, Yong Qiang Wang, Juan Wen, Valdez A. James, Kurt E. Sickafus
Ho2O3 and TiO2 powders were used in the molar ratios of 1:2, 3:4 and 1:1 to produce sintered oxide pellets of composition Ho2+xTi2-xO7-x/2 (x=0, 0.4 and 0.67) (or Ho2Ti2O7, Ho1.5TiO4.25 and Ho2TiO5), respectively.
Results and discussions Fig.1.
References [1] R.C.
Alloys and Compounds. 479 (2009) 6-10
Lett. 28 (2011), 066102(1)-066102(4).
Results and discussions Fig.1.
References [1] R.C.
Alloys and Compounds. 479 (2009) 6-10
Lett. 28 (2011), 066102(1)-066102(4).
Online since: September 2014
Authors: Jin Sha Yuan, Zhong Li, Ke Zhang, Wei Hua Zhang
A Reasoning Method of Transformer Fault Causes Based on Fuzzy Petri Net
Weihua Zhang 1,a, Jinsha Yuan 1, Ke Zhang1, Zhong Li 1
1 School of Electrical and Electronic Engineering, North China Electric Power University, China
azwhhdbd@126.com
Keywords: fuzzy Petri net, transformer, fault causes reasoning, production rule.
According to Reference [11], the analysis on causes of overheating fault is shown in Table 1.
References [1] X.
Power System Technology, Vol.32,No.1,(2008),p.46-50
The analysis and processing of iron core multipoint earthing fault on No. 1 Main Transformer in 110kV substation.
According to Reference [11], the analysis on causes of overheating fault is shown in Table 1.
References [1] X.
Power System Technology, Vol.32,No.1,(2008),p.46-50
The analysis and processing of iron core multipoint earthing fault on No. 1 Main Transformer in 110kV substation.
Online since: March 2007
Authors: Heng Zhi Fu, X.P. Guo, Ping Guan, K. Kusabiraki, L.M. Gao
Gao
1,b
, P.
Figure 1 presents the X-ray diffractogram of Fig. 1 X-ray diffractogram of the master alloy.
The composition of the area labeled with "2" is 64.5Nb- 22.4Ti- 1.8Si- 1.7Hf- 3.0Cr- 6.6Al, so the phase should be Nbss.
References [1] B.P.
Forum Vols. 475-479 (2005), p. 745.
Figure 1 presents the X-ray diffractogram of Fig. 1 X-ray diffractogram of the master alloy.
The composition of the area labeled with "2" is 64.5Nb- 22.4Ti- 1.8Si- 1.7Hf- 3.0Cr- 6.6Al, so the phase should be Nbss.
References [1] B.P.
Forum Vols. 475-479 (2005), p. 745.