Abstract: Growth of 4H-SiC epitaxial layers has been performed in a horizontal hot-wall CVD (chemical vapor deposition) reactor using the silane-propane-hydrogen system. Two inch 4H-SiC, C-face wafers with an off-cut angle of about 7° towards <11 2 0> direction have been used as substrates. Micropipe dissociation has been investigated by varying the carbon-silicon (C/Si) ratio in the source gas atmosphere. Depending on the C/Si ratio the micropipes propagate into the layer without changing their image (C/Si > 1) or they dissociate in separate dislocations leaving a scar like formed surface region (C/Si £ 1). The substrates including epitaxial layers of reduced micropipe density were used as seeds for bulk crystal growth. If a micropipe is once closed in an epilayer grown at a low C/Si ratio, it is not opened in the subsequent growth process at high temperature.

Abstract: Planar defects have been found in nitrogen doped 2" 4H-SiC crystals grown on off-axis seeds. The doping level was 1×1019cm-3, which is below the critical one for the thermally activated cubic stacking fault formation in the 4H matrix. Planar defects in the doped region are nucleated on the whole seed surface outside the growth facet. They are coexisting 15R and 6H lamellas of unitcell height as revealed by means of luminescence and high resolution transmission electron microscopy. These inclusions are preferably formed at the rim of the growth facet, where polytype change occurs after switching off the nitrogen flow during growth.