Preparation and Characterization of Flexible Polyurethane Foams from Palm Oil-Based Polyol

Abstract:

Flexible polyurethane (PU) foams were prepared by replacing commercial petroleum-based polyether polyol with palm oil-based polyol up to 50 wt%. Palm oil was converted to polyol by transesterification reaction with glycerol using calcium oxide as a catalyst. PU foams were then prepared from reaction between mixtures of palm oil-based polyol and petrochemical polyols with toluene diisocyanate (TDI) using water as blowing agent. The morphology and physical-mechanical properties including apparent density, indentation hardness, compressive deflection coefficient or support factor, tensile strength, and tear strength of the prepared foams were characterized and compared to those of reference foam prepared using only conventional petrochemical polyols. Scanning electron microscopy (SEM) indicated that the cellular structures of all the prepared foams were semi-open and the cell size decreased with higher amount of palm oil-based polyol. The apparent densities and the compressive deflection coefficient of the PU foams increased with the increasing amount of palm oil-based polyol, while the indentation hardness showed the opposite tendency. Furthermore, the obtained foam modified with palm oil-based polyol of 20 wt% were found to have the highest tensile and tear strengths.

• Periodical: Advanced Materials Research (Volume 911)
• Pages: 352-356
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.911.352
• Online since: March 2014
• Authors: Duangphon Lumcharoen, Onusa Saravari
• Keywords: Flexible Polyurethane Foam, Palm Oil, Polyol, Transesterification

References

[1] R. Herrington, R. Turner, and W. Lidy, in: Flexible Foam Fundamentals, edited by R. Herrington and K. Hock, Flexible Polyurethane Foams, chapter, 3, The Dow Chemical Company, United States of America, (1997).

[2] M. F. Valero and A. Gonzalez, Polyurethane Adhesive System from Castor Oil Modified by a Transesterification Reaction, Journal of Elastomers and Plastics, 44 (2012), pp.433-442.

DOI: 10.1177/0095244312437155

[3] S. Chuayjuljit, T. Sangpakdee, and O. Saravari, Processing and Properties of Palm Oil-based Rigid Polyurethane Foam, Journal of Metals, Materials and Minerals, 17 (2007), pp.17-23.

[4] R. Tanaka, S. Hirose, and H. Hatakeyama, Preparation And Characterization of Polyurethane Foams Using a Palm Oil-based Polyol, Bioresource Technology, 99 (2008), pp.3810-3816.

DOI: 10.1016/j.biortech.2007.07.007

[5] S. Das, M. Dave, and G. L. Wilkes, Characterization of Flexible Polyurethane Foams based on Soybean-based Polyols, Journal of Applied Polymer Science, 112 (2009), pp.299-308.

DOI: 10.1002/app.29402

[6] H. Pawlik and A. Prociak, Influence of Palm Oil-based Polyol on the Properties of Flexible Polyurethane Foams, Journal of Polymers and the Environment, 20 (2012), pp.438-445.

DOI: 10.1007/s10924-011-0393-2

[7] Dr. Fyodor and A. Shutov, in: Cellular Structure and Properties of Foamed Polymers, edited by D. Klempner and K. C. Frish, Handbook of Polymeric Foams and Foam Technology, chapter 3, Hanser, Germany, (1991).

[8] G. Woods, The ICI polyurethanes book, ICI Polyurethanes and John Wiley & Sons, The Netherlands, (1987).

DOI: 10.1016/0032-3861(88)90034-1

[9] K. Hock, R. Priester, R. Herrington, G. Wiltz, and JR., L. Jeng, in: Evaluation and Testing, edited by R. Herrington and K. Hock, Flexible Polyurethane Foams, chapter, 7, The Dow Chemical Company, United States of America, (1997).

DOI: 10.1201/9780203506141.ch6