Paper Titles
Effects of Wetting Behavior on Gallium Addition in In-Zn Solder Alloy
p.22
The Alloying and Aging Effects on the Wettability and Intermetallic Bonding of the Sn-Zn-Cu-Bi Soldering Alloy on a Cu Substrate
p.26
Nanoindentation Study on Heat Treated Gold Wire Bonding
p.31
Directional Growth Behaviour of Intermetallic Compound of Sn3.0Ag0.5Cu/ImSn Subjected to Thermal Cycling
p.36
Nanoindentation of Sn3.0Ag0.5Cu/ENIG Solder Joint after High Temperature Storage
p.40
Solidification of Sn-3Ag-0.5Cu and Sn-0.7Cu-0.05Ni Solders
p.44
Effects of Trace Phosphorus in Sn-Cu-Ni Wave Solder Dross
p.49
Suppression of Cu3Sn with Ni in High Cu Containing Sn-Cu Solder Alloys
p.53
Peritectic Reactions and Phase Transformations of Sn-30wt%Cu for High Temperature Pb-Free Soldering Applications
p.58

Nanoindentation of Sn3.0Ag0.5Cu/ENIG Solder Joint after High Temperature Storage

Article Preview

Abstract:

This study used nanoindentation technique in order to examine the micromechanical properties of Sn3.0Ag0.5Cu (SAC305) on Electroless Nickel Immersion Gold (ENIG) surface finished Cu substrate subjected to high temperature storage. Lead free solder paste of SAC305 were soldered on ENIG substrate by reflow soldering at 215 °C for 8 second. The soldered samples were exposed to high temperature storage at 180 °C for 0, 200, 400, 600, 800 and 1000 hours. Micromechanical properties show that the solder hardness is decreasing with the HTS time from 239.13 MPa for 0 hour to 178.96 MPa for 1000 hours while the reduce modulus results has increased from 62. 16 x 103 MPa for 0 hour to 82.13 x 103 MPa for 1000 hours. The value of hardness and reduced modulus from nanoindentation approach indicate the occurrence of plastic and elastic deformation throughout the test.

You might also be interested in these eBooks
Advanced Materials Engineering and Technology IV View Preview

Info:

Periodical:

Materials Science Forum (Volume 857)

Pages:

40-43

DOI:

https://doi.org/10.4028/www.scientific.net/MSF.857.40

Citation:

Cite this paper

Online since:

May 2016

Authors:

Maria Abu Bakar, Azman Jalar*, Roslina Ismail, Abdul Razak Daud

Keywords:

ENIG, High Temperature Storage, Lead Free Solder, Mechanical Properties, SAC305

Export:

RIS, BibTeX

Price:

Permissions CCC:

Request Permissions

Permissions PLS:

Request Permissions

Сopyright:

© 2016 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

* - Corresponding Author

References

[1] T. An and F. Qin: Microelectron. Reliab. Vol. 54 (2014), p.932.

Google Scholar

[2] W.Y.W. Yusoff, R. Ismail, A. Jalar, N.K. Othman and I.A. Rahman: Mater. Charac. Vol. 93 (2014), p.129.

Google Scholar

[3] M.N. Zulkifli, A. Jalar, S. Abdullah, I.A. Rahman and M.A.A. Hamid: Mater. Sci. Eng. A Vol. 577 (2013), p.189.

Google Scholar

[4] M.N. Zulkifli, A. Jalar, S. Abdullah, I.A. Rahman and N.K. Othman: J. Electron. Mater. Vol. 42 (6) (2013), p.1063.

Google Scholar

[5] Y. Hang, G. Liu, K. Huang and W. Jin: J. Membr. Sci Vol. 494 (2015), p.205.

Google Scholar

[6] J.J. Roa, G. Fargas, A. Mateo and E.J. Pigue: Mater. Sci. Eng. A Vol. 645 (2015), p.188.

Google Scholar

[7] W.C. Oliver and G.M. Pharr: J. Mater. Research Vol. 7(06) (1992), p.1564.

Google Scholar

[8] Y. Rosenthal, A. Stern, S.R. Cohen and D. Eliezer: Mater. Sci. Eng. A Vol. 527 (2010), p.4014.

Google Scholar

© 2025 Trans Tech Publications Ltd. All rights are reserved, including those for text and data mining, AI training, and similar technologies. For open access content, terms of the Creative Commons licensing CC-BY are applied.
Scientific.Net is a registered trademark of Trans Tech Publications Ltd.