Effect of Sintering Temperature on Structure and Dielectric Properties of BZN Ceramics

Abstract:

Bismuth zinc niobate [(Bi_1.5Zn_0.5)(Nb_1.5Zn_0.5)O₇, abbreviated as BZN] ceramics are receiving increasing attention due to their excellent dielectric properties in the microwave frequency range. This work is aimed at improving the fabrication technology of BZN ceramics. BZN ceramic specimens were prepared using the general electronic ceramic technique including milling, calcining, crushing, pressing, and sintering. Different sintering temperatures in the range of 950-1080°C were used to study how sintering temperature affects the structure and dielectric properties of BZN ceramics. The crystallinity and microstructure of the BZN ceramics, which were measured respectively by X-ray diffraction and scanning electron microscopy, were improved with increasing of the sintering temperature. The frequency dependence of the dielectric constant and loss tangent was measured at room temperature from 1 kHz to 1 MHz. The dielectric properties of the specimen sintered at 1050°C were found to be the best, for which the relative permittivity (ε_r) and the loss tangent (tanδ) are around 146 and 0.005, respectively. It was also foεund that when the sintering temperature was higher than 1000°C, the ε_r and the tanδ of BZN ceramics sintered at different temperatures were similar. As a result, 1000°C may be an appropriate sintering temperature for BZN ceramics.

• Periodical: Key Engineering Materials (Volumes 512-515)
• Pages: 1203-1206
• DOI: https://doi.org/10.4028/www.scientific.net/KEM.512-515.1203
• Online since: June 2012
• Authors: Yun Hui Xu, Xiao Hong Zhu, Qiang Zhang, Jian Guo Zhu, Ding Quan Xiao
• Keywords: Crystal Structure, Dielectric Property, Sintering Temperature

References

[1] D.P. Can, C.A. Randall, T.R. Shrout, Investigation of the dielectric properties of bismuth pyrochlores, Solid State Commun. 7 (1996)529–534.

DOI: 10.1016/0038-1098(96)00012-9

[2] Z.P. Wang, S.Y. Zhang, No lead low-fired multilayer ceramic capacitor (MLC) dielectric materials, Electron. Compon. Mater.(Chin.). 1(1)(1979)11-18.

[3] X.L. Wang, et al., Structures, phase transformations, and dielectric properties of pyrochlores containing bismuth, J. Am. Ceram. Soc. 80[10](1997)2745-48.

[4] K. Sudheendran, K.C. James Raju, Temperature-dependent dielectric, impedance and tunability studies on bismuth zinc niobate ((Bi1.5Zn0.5)(Nb1.5Zn0.5)O7) ceramics, Ceramics International. 34 (2008) 897-900.

DOI: 10.1016/j.ceramint.2007.09.055

[5] A.R. West, D.C. Sinclair, N. Hirose, Charecterization of electrical materials, especially ferroelectrics by impedance spectroscopy, J. Electroceram. 1(1)(1997)65-71.

[6] M.E. Lines, et al., Principle and Applications of Ferroelectric Materials, Clarendon Press, Oxford. 1977, p.102.

[7] H. Wang, et al., Bismuth zinc niobate (Bi1.5ZnNb1.5O7) ceramics derived from metallo-organic decomposition precursor solution, Solid State Communications. 132(2004) 481-486.

DOI: 10.1016/j.ssc.2004.07.071